Dimethylformamide (DMF), a polar solvent, is commonly used for preparing graphene/epoxy nanocomposites. While commonly previous research has predominantly highlighted the improvement in physio-mechanical properties of these nanocomposites, the effect of DMF on processing and its direct influence on the final characteristics of MXene/epoxy nanocomposites have not been investigated.This unexplored link between DMF dosage, MXene concentrations, and the final composite properties presents an exciting direction for future research. In this study, a fixed dosage of DMF was used with varying MXene concentrations to fabricate the nanocomposites. To assess the reliability of DMF dosage on the characteristics of the fabricated nanocomposites, various evaluation techniques were employed, including dispersion evaluation, mechanical tests, thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), scanning electron microscopy (SEM), electromagnetic interference (EMI) shielding, and surface roughness measurements. The research outcomes revealed that as MXene concentration increased, the characteristics of the MXene/epoxy nanocomposites, improved across the board, indicating their potential for use in energy storage applications.

The influence of short term water absorption on the mechanical properties of halloysite nanotubes-multi layer graphene reinforced polyester hybrid nanocomposites has been investigated. The addition of nano-fillers significantly increased the flexural strength; tensile strength and impact strength in dry and wet conditions. After short term water exposure; the maximum microhardness; tensile; flexural and impact toughness values were observed at 0.1 wt% MLG. The microhardness increased up to 50.3%; tensile strength increased up to 40% and flexural strength increased up to 44%. Compared to dry samples; the fracture toughness and surface roughness of all types of produced nanocomposites were increased that may be attributed to plasticization effect. Scanning electron microscopy revealed that the main failure mechanism is caused by the weakening of nano-filler-matrix interface induced by water absorption. It was further observed that synergistic effects were not effective at concentration of 0.1 wt% to produce considerable improvement in mechanical properties of produced hybrid nanocomposites.