Durability of MgO/hydromagnesite mortars -- Resistance to chlorides and corrosion
Authors:
Fabio Enrico Furcas,
Alexander German,
Frank Winnefeld,
Pietro Lura,
Ueli Angst
Abstract:
The durability of MgO/hydromagnesite mortars was studied with respect to their corrosion performance and resistance to chloride attack and moisture. MgO/hydromagnesite pastes were cured in chloride solution to induce potential formation of Mg-chlorides; however, no such phases were observed. Rapid chloride ingress measurements demonstrated high penetration resistance and low chloride migration coe…
▽ More
The durability of MgO/hydromagnesite mortars was studied with respect to their corrosion performance and resistance to chloride attack and moisture. MgO/hydromagnesite pastes were cured in chloride solution to induce potential formation of Mg-chlorides; however, no such phases were observed. Rapid chloride ingress measurements demonstrated high penetration resistance and low chloride migration coefficients, i.e. D_Cl = 1e-13 to 1e-12 m^2/s. The corrosion rate of carbon steel embedded in MgO/HY mortars, as determined by linear polarization resistance measurements, was in the range icorr = 1e-9 A/cm^2 in dry and 1e-7 A/cm^2 in wet conditions, irrespective of the mortar composition or curing condition.These findings corroborate the hypothesis that, in the absence of chlorides, the moisture condition is the primary predictor of corrosion rate of carbon steel in the MgO/hydromagnesite binder. These accelerated, short-term experiments suggest that the binder may be suited to protect embedded carbon steel from corrosion under specific exposure conditions of practical relevance.
△ Less
Submitted 13 May, 2024;
originally announced May 2024.
Alkali-silica reaction products and cracks: X-ray micro-tomography-based analysis of their spatial-temporal evolution at a mesoscale
Authors:
Mahdieh Shakoorioskooie,
Michele Griffa,
Andreas Leemann,
Robert Zboray,
Pietro Lura
Abstract:
In this study, we propose a laboratory-scale methodology, based on X-ray micro-tomography and caesium (Cs) as a contrast agent, to advance the understanding of cracking due to alkali-silica reaction (ASR) in concrete. The methodology allows achieving a completely non-destructive and time-lapse characterization of the spatial-temporal patterns of both the cracks and the ASR products. While Cs addit…
▽ More
In this study, we propose a laboratory-scale methodology, based on X-ray micro-tomography and caesium (Cs) as a contrast agent, to advance the understanding of cracking due to alkali-silica reaction (ASR) in concrete. The methodology allows achieving a completely non-destructive and time-lapse characterization of the spatial-temporal patterns of both the cracks and the ASR products. While Cs addition slightly accelerated the ASR kinetics, the crack pat-terns, with and without Cs addition, were statistically equivalent. Cracks with ASR products appeared first in the aggregates, close to the interface with the cement paste. They propagated afterwards towards the aggregates interior. Some products were then extruded for several mm into air voids and cracks in the cement paste. This process suggests that, in the early stage, the ASR products may be a low-viscosity gel that can flow away from the source aggregate and may settle later elsewhere as a rigid phase, upon calcium uptake.
△ Less