Magnetic nanofibers for remotely triggered catalytic activity applied to the degradation of organic pollutants
Authors:
Jesús A. Fuentes-García,
Beatriz Sanz-Sagué,
Reyes Mallada,
M. Ricardo Ibarra,
Gerardo F. Goya
Abstract:
This work reports on the synthesis and characterization of a new type of electrospun magnetic nanofibers (MNFs), and their application for degradation of organic pollutants using remote magnetic inductive heating. We describe a simple protocol combining a fast (app. 5 min) synthesis of MnFe\textsubscript{2}O\textsubscript{4} magnetic nanoparticles (MNPs) by sonochemical route, optimized for induct…
▽ More
This work reports on the synthesis and characterization of a new type of electrospun magnetic nanofibers (MNFs), and their application for degradation of organic pollutants using remote magnetic inductive heating. We describe a simple protocol combining a fast (app. 5 min) synthesis of MnFe\textsubscript{2}O\textsubscript{4} magnetic nanoparticles (MNPs) by sonochemical route, optimized for inductive heating, with their subsequent incorporation in electrospun MNFs composed of polyacrylonitrile (PAN) nanofibers. The resulting multifunctional MNFs (average diameter $φ= 760 \pm 150$ nm) contain up to $\approx 30%$wt. of the MNPs. The composite showed superhydrophobic behaviour ($θ_c = 165^\circ$) and a band gap value of 1.75 eV. We found that the presence of MNPs embedded into the polymeric nanofibers modify the exothermic and the glass transitions temperatures compared with pure PAN nanofibers, suggesting a strong attachment between MNPs and polymeric chains. The MNFs could be remotely activated by alternating magnetic fields (AMF, $f = 200-800$ kHz, $H_0 = 10-36$ kA/m) for accelerating the catalytic reactions of the organic dye methylene blue (MB). A remarkable stability of the MNFs against degradation under extreme pH conditions ($3<pH<10$) resulted in a sustained heating efficiency after many heating cycles. We observed a degradation efficiency $>80%$ in the presence of hydrogen peroxide under AMFs, attributed to Fe\textsuperscript{2+}/\textsuperscript{3+} and Mn\textsuperscript{2+}/\textsuperscript{3+}/\textsuperscript{4+} active centers on the surface of the MNP/MNFs observed from XPS data. The capacity of these materials for magnetic remote activation appeals catalytic applications under conditions of darkness or restrained access, where no photocatalytic reactions can be achieved.
△ Less
Submitted 26 March, 2023;
originally announced March 2023.
-
Low Dimensional Assemblies of Magnetic MnFe$_2$O$_4$ Nanoparticles and Direct In Vitro Measurements of Enhanced Heating Driven by Dipolar Interactions: Implications for Magnetic Hyperthermia
Authors:
Beatriz Sanz,
Rafael Cabreira-Gomes,
Teobaldo E. Torres,
Daniela P. Valdés,
Enio Lima Jr.,
Emilio De Biasi,
Roberto D. Zysler,
M. Ricardo Ibarra,
Gerardo F. Goya
Abstract:
Magnetic fluid hyperthermia (MFH), the procedure of raising the temperature of tumor cells using magnetic nanoparticles (MNPs) as heating agents, has proven successful in treating some types of cancer. However, the low heating power generated under physiological conditions makes necessary a high local concentration of MNPs at tumor sites. Here, we report how the in vitro heating power of magnetica…
▽ More
Magnetic fluid hyperthermia (MFH), the procedure of raising the temperature of tumor cells using magnetic nanoparticles (MNPs) as heating agents, has proven successful in treating some types of cancer. However, the low heating power generated under physiological conditions makes necessary a high local concentration of MNPs at tumor sites. Here, we report how the in vitro heating power of magnetically soft MnFe$_2$O$_4$ nanoparticles can be enhanced by intracellular low-dimensional clusters through a strategy that includes: a) the design of the MNPs to retain Néel magnetic relaxation in high viscosity media, and b) culturing MNP-loaded cells under magnetic fields to produce elongated intracellular agglomerates. Our direct in vitro measurements demonstrated that the specific loss power (SLP) of elongated agglomerates ($SLP=576\pm33$ W/g) induced by culturing BV2 cells in situ under a dc magnetic field was increased by a factor of 2 compared to the $SLP=305\pm25$ W/g measured in aggregates freely formed within cells. A numerical mean-field model that included dipolar interactions quantitatively reproduced the SLPs of these clusters both in phantoms and in vitro, suggesting that it captures the relevant mechanisms behind power losses under high-viscosity conditions. These results indicate that in situ assembling of MNPs into low-dimensional structures is a sound possible way to improve the heating performance in MFH.
△ Less
Submitted 15 November, 2020;
originally announced November 2020.
-
Disordered hyperuniformity in superconducting vortex lattices
Authors:
Jose Benito-Llorens,
Isabel Guillamón,
Ismael García-Serrano,
Rosa Córdoba,
Javier Sesé,
José María De Teresa,
M. Ricardo Ibarra,
Sebastián Vieira,
Miguel Ortuño,
Hermann Suderow
Abstract:
Particles occupying sites of a random lattice present density fluctuations at all length scales. It has been proposed that increasing interparticle interactions reduces long range density fluctuations, deviating from random behaviour. This leads to power laws in the structure factor and the number variance that can be used to characterize deviations from randomness which eventually lead to disorde…
▽ More
Particles occupying sites of a random lattice present density fluctuations at all length scales. It has been proposed that increasing interparticle interactions reduces long range density fluctuations, deviating from random behaviour. This leads to power laws in the structure factor and the number variance that can be used to characterize deviations from randomness which eventually lead to disordered hyperuniformity. It is not yet fully clear how to link density fluctuations with interactions in a disordered hyperuniform system. Interactions between superconducting vortices are very sensitive to vortex pinning, to the crystal structure of the superconductor and to the value of the magnetic field. This creates lattices with different degrees of disorder. Here we study disordered vortex lattices in several superconducting compounds (Co-doped NbSe$_2$, LiFeAs and CaKFe$_4$As$_4$) and in two amorphous W-based thin films, one with strong nanostructured pinning (W-film-1) and another one with weak or nearly absent pinning (W-film-2). We calculate for each case the structure factor and number variance and compare to calculations on an interacting set of partially pinned particles. We find that random density fluctuations appear when pinning overcomes interactions and show that the suppression of density fluctuations is indeed correlated to the presence of interactions. Furthermore, we find that we can describe all studied vortex lattices within a single framework consisting of a continous deviation from hyperuniformity towards random distributions when increasing the strength of pinning with respect to the intervortex interaction.
△ Less
Submitted 24 February, 2020;
originally announced February 2020.
-
Interface-induced anomalous Nernst effect in Fe3O4/Pt-based heterostructures
Authors:
R. Ramos,
T. Kikkawa,
A. Anadón,
I. Lucas,
T. Niizeki,
K. Uchida,
P. A. Algarabel,
L. Morellón,
M. H. Aguirre,
M. R. Ibarra,
E. Saitoh
Abstract:
We have studied the anomalous Nernst effect (ANE) in [Fe3O4/Pt]-based heterostructures, by measuring the ANE-induced electric field with a magnetic field applied normal to the sample surface, in the perpendicular magnetized configuration, where only the ANE is expected. An ANE voltage is observed for [Fe3O4/Pt]n multilayers, and we further investigated its origin by performing measurements in [Fe3…
▽ More
We have studied the anomalous Nernst effect (ANE) in [Fe3O4/Pt]-based heterostructures, by measuring the ANE-induced electric field with a magnetic field applied normal to the sample surface, in the perpendicular magnetized configuration, where only the ANE is expected. An ANE voltage is observed for [Fe3O4/Pt]n multilayers, and we further investigated its origin by performing measurements in [Fe3O4/Pt/Fe3O4] trilayers as a function of the Pt thickness. Our results suggest the presence of an interface-induced ANE. Despite of this ANE, the spin Seebeck effect is the dominant mechanism for the transverse thermoelectric voltage in the in-plane magnetized configuration, accounting for about 70 % of the measured voltage in the multilayers.
△ Less
Submitted 28 September, 2018;
originally announced September 2018.
-
Quantifying the leading role of the surface state in the Kondo effect of Co/Ag(111)
Authors:
M. Moro-Lagares,
J. Fernández,
P. Roura-Bas,
M. R. Ibarra,
A. A. Aligia,
D. Serrate
Abstract:
Using a combination of scanning tunneling spectroscopy and atomic lateral manipulation, we obtained a systematic variation of the Kondo temperature ($T_\mathrm K$) of Co atoms on Ag(111) as a function of the surface state contribution to the total density of states at the atom adsorption site ($ρ_s$). By sampling the $T_\mathrm K$ of a Co atom on positions where $ρ_s$ was spatially resolved before…
▽ More
Using a combination of scanning tunneling spectroscopy and atomic lateral manipulation, we obtained a systematic variation of the Kondo temperature ($T_\mathrm K$) of Co atoms on Ag(111) as a function of the surface state contribution to the total density of states at the atom adsorption site ($ρ_s$). By sampling the $T_\mathrm K$ of a Co atom on positions where $ρ_s$ was spatially resolved beforehand, we obtain a nearly linear relationship between both magnitudes. We interpret the data on the basis of an Anderson model including orbital and spin degrees of freedom (SU(4)) in good agreement with the experimental findings. The fact that the onset of the surface band is near the Fermi level is crucial to lead to the observed linear behavior. In the light of this model, the quantitative analysis of the experimental data evidences that at least a quarter of the coupling of Co impurities with extended states takes place through the hybridization to surface states. This result is of fundamental relevance in the understanding of Kondo screening of magnetic impurities on noble metal surfaces, where bulk and surface electronic states coexist.
△ Less
Submitted 4 July, 2018;
originally announced July 2018.
-
Terahertz spin currents and inverse spin Hall effect in thin-film heterostructures containing complex magnetic compounds
Authors:
T. Seifert,
U. Martens,
S. Günther,
M. A. W. Schoen,
F. Radu,
X. Z. Chen,
I. Lucas,
R. Ramos,
M. H. Aguirre,
P. A. Algarabel,
A. Anadón,
H. Körner,
J. Walowski,
C. Back,
M. R. Ibarra,
L. Morellón,
E. Saitoh,
M. Wolf,
C. Song,
K. Uchida,
M. Münzenberg,
I. Radu,
T. Kampfrath
Abstract:
Terahertz emission spectroscopy of ultrathin multilayers of magnetic and heavy metals has recently attracted much interest. This method not only provides fundamental insights into photoinduced spin transport and spin-orbit interaction at highest frequencies but has also paved the way to applications such as efficient and ultrabroadband emitters of terahertz electromagnetic radiation. So far, predo…
▽ More
Terahertz emission spectroscopy of ultrathin multilayers of magnetic and heavy metals has recently attracted much interest. This method not only provides fundamental insights into photoinduced spin transport and spin-orbit interaction at highest frequencies but has also paved the way to applications such as efficient and ultrabroadband emitters of terahertz electromagnetic radiation. So far, predominantly standard ferromagnetic materials have been exploited. Here, by introducing a suitable figure of merit, we systematically compare the strength of terahertz emission from X/Pt bilayers with X being a complex ferro-, ferri- and antiferromagnetic metal, that is, dysprosium cobalt (DyCo$_5$), gadolinium iron (Gd$_{24}$Fe$_{76}$), Magnetite (Fe$_3$O$_4$) and iron rhodium (FeRh). We find that the performance in terms of spin-current generation not only depends on the spin polarization of the magnet's conduction electrons but also on the specific interface conditions, thereby suggesting terahertz emission spectroscopy to be a highly surface-sensitive technique. In general, our results are relevant for all applications that rely on the optical generation of ultrafast spin currents in spintronic metallic multilayers.
△ Less
Submitted 14 July, 2021; v1 submitted 31 May, 2017;
originally announced May 2017.
-
On the nature of the (de)coupling of the magnetostructural transition in Er$_5$Si$_4$
Authors:
Rui M. Costa,
João H. Belo,
Marcelo B. Barbosa,
Pedro A. Algarabel,
César Magén,
Luis Morellon,
Manuel R. Ibarra,
João N. Gonçalves,
Nuno M. Fortunato,
João S. Amaral,
João P. Araújo,
André M. Pereira
Abstract:
In this report, a successful thermodynamical model was employed to understand the structural transition in Er$_5$Si$_4$, able to explain the decoupling of the magnetic and structural transition. This was achieved by the DFT calculations which were used to determine the energy differences at 0 K, using a LSDA+U approximation. It was found that the M structure as the stable phase at low temperatures…
▽ More
In this report, a successful thermodynamical model was employed to understand the structural transition in Er$_5$Si$_4$, able to explain the decoupling of the magnetic and structural transition. This was achieved by the DFT calculations which were used to determine the energy differences at 0 K, using a LSDA+U approximation. It was found that the M structure as the stable phase at low temperatures as verified experimentally with a $ΔF_0 = -$0.262 eV. Finally, it was achieved a variation of Seebeck coefficient ($\sim$ 6 $μ$V) at the structural transition which allow to conclude that the electronic entropy variation is negligible in the transition.
△ Less
Submitted 24 August, 2017; v1 submitted 31 March, 2017;
originally announced March 2017.
-
Magnetic hyperthermia enhances cell toxicity with respect to exogenous heating
Authors:
Beatriz Sanz,
M. Pilar Calatayud,
Teobaldo E. Torres,
Mónica L. Fanarraga,
M. Ricardo Ibarra,
Gerardo F. Goya
Abstract:
Magnetic hyperthermia is a new type of cancer treatment designed for overcoming resistance to chemotherapy during the treatment of solid, inaccessible human tumors. The main challenge of this technology is increasing the local tumoral temperature with minimal side effects on the surrounding healthy tissue. This work consists of an in vitro study that compared the effect of hyperthermia in response…
▽ More
Magnetic hyperthermia is a new type of cancer treatment designed for overcoming resistance to chemotherapy during the treatment of solid, inaccessible human tumors. The main challenge of this technology is increasing the local tumoral temperature with minimal side effects on the surrounding healthy tissue. This work consists of an in vitro study that compared the effect of hyperthermia in response to the application of exogenous heating (EHT) sources with the corresponding effect produced by magnetic hyperthermia (MHT) at the same target temperatures. Human neuroblastoma SH-SY5Y cells were loaded with magnetic nanoparticles (MNPs) and packed into dense pellets to generate an environment that is crudely similar to that expected in solid micro-tumors, and the above-mentioned protocols were applied to these cells. These experiments showed that for the same target temperatures, MHT induces a decrease in cell viability that is larger than the corresponding EHT, up to a maximum difference of approximately 45\% at T = 46°C. An analysis of the data in terms of temperature efficiency demonstrated that MHT requires an average temperature that is 6°C lower than that required with EHT to produce a similar cytotoxic effect. An analysis of electron microscopy images of the cells after the EHT and MHT treatments indicated that the enhanced effectiveness observed with MHT is associated with local cell destruction triggered by the magnetic nano-heaters. The present study is an essential step toward the development of innovative adjuvant anti-cancer therapies based on local hyperthermia treatments using magnetic particles as nano-heaters.
△ Less
Submitted 7 November, 2016;
originally announced November 2016.
-
Long term stability and reproducibility of magnetic colloids are key issues for steady values of Specific Power Absorption through time
Authors:
B. Sanz,
M. P. Calatayud,
N. Cassinelli,
M. R. Ibarra,
G. F. Goya
Abstract:
Virtually all clinical applications of magnetic nanoparticles (MNPs) require the formulation of biocompatible, water-based magnetic colloids. For magnetic hyperthermia, the requirements also include a high colloidal stability against precipitation and agglomeration of the constituent MNPs, in order to keep the heating efficiency of the ferrofluid in the long term. The specific power absorption (SP…
▽ More
Virtually all clinical applications of magnetic nanoparticles (MNPs) require the formulation of biocompatible, water-based magnetic colloids. For magnetic hyperthermia, the requirements also include a high colloidal stability against precipitation and agglomeration of the constituent MNPs, in order to keep the heating efficiency of the ferrofluid in the long term. The specific power absorption (SPA) of single-domain MNPs depends critically on the average particle size and size distribution width, therefore first-rate reproducibility among different batches regarding these parameters are also needed. We have studied the evolution of the SPA of highly reproducible and stable water-based colloid composed of polymer coated $Fe_{3}O_{4}$ magnetic nanoparticles. By measuring the specific power absorption (SPA) values along one year as a function of field amplitude and frequencies ($H \leq 24 kA/m$; $260 \leq f \leq 830 kHz$), we demonstrated that SPA in these samples can be made reproducible between successive synthesis, and stable along several months, due to the in situ polymer coating that provides colloidal stability and keeps dipolar interactions negligible.
△ Less
Submitted 25 August, 2016;
originally announced September 2016.
-
Thermoelectric performance of spin Seebeck effect in Fe3O4/Pt-based thin film heterostructures
Authors:
R. Ramos,
A. Anadon,
I. Lucas,
K. Uchida,
P. A. Algarabel,
L. Morellon,
M. H. Aguirre,
E. Saitoh,
M. R. Ibarra
Abstract:
We report a systematic study on the thermoelectric performance of spin Seebeck devices based on Fe3O4/Pt junction systems. We explore two types of device geometries: a spin Hall thermopile and spin Seebeck multilayer structures. The spin Hall thermopile increases the sensitivity of the spin Seebeck effect, while the increase in the sample internal resistance has a detrimental effect on the output…
▽ More
We report a systematic study on the thermoelectric performance of spin Seebeck devices based on Fe3O4/Pt junction systems. We explore two types of device geometries: a spin Hall thermopile and spin Seebeck multilayer structures. The spin Hall thermopile increases the sensitivity of the spin Seebeck effect, while the increase in the sample internal resistance has a detrimental effect on the output power. We found that the spin Seebeck multilayers can overcome this limitation since the multilayers exhibit the enhancement of the thermoelectric voltage and the reduction of the internal resistance simultaneously, therefore resulting in significant power enhancement. This result demonstrates that the multilayer structures are useful for improving the thermoelectric performance of the spin Seebeck effect.
△ Less
Submitted 12 May, 2016;
originally announced May 2016.
-
Validity of the Néel-Arrhenius model for highly anisotropic Co_xFe_{3-x}O_4 nanoparticles
Authors:
T. E. Torres,
E. Lima Jr.,
A. Mayoral,
A. Ibarra,
C. Marquina,
M. R. Ibarra,
G. F. Goya
Abstract:
We report a systematic study on the structural and magnetic properties of Co_{x}Fe_{3-x}O_{4} magnetic nanoparticles with sizes between $5$ to $25$ nm, prepared by thermal decomposition of Fe(acac)_{3} and Co(acac)_{2}. The large magneto-crystalline anisotropy of the synthesized particles resulted in high blocking temperatures ($42$ K \leqq $T_B$ $\leqq 345$ K for $5 \leqq$ d $\leqq 13$ nm ) and l…
▽ More
We report a systematic study on the structural and magnetic properties of Co_{x}Fe_{3-x}O_{4} magnetic nanoparticles with sizes between $5$ to $25$ nm, prepared by thermal decomposition of Fe(acac)_{3} and Co(acac)_{2}. The large magneto-crystalline anisotropy of the synthesized particles resulted in high blocking temperatures ($42$ K \leqq $T_B$ $\leqq 345$ K for $5 \leqq$ d $\leqq 13$ nm ) and large coercive fields ($H_C \approxeq 1600$ kA/m for $T = 5$ K). The smallest particles ($<d>=5$ nm) revealed the existence of a magnetically hard, spin-disordered surface. The thermal dependence of static and dynamic magnetic properties of the whole series of samples could be explained within the Néel-Arrhenius relaxation framework without the need of ad-hoc corrections, by including the thermal dependence of the magnetocrystalline anisotropy constant $K_1(T)$ through the empirical Brükhatov-Kirensky relation. This approach provided $K_1(0)$ values very similar to the bulk material from either static or dynamic magnetic measurements, as well as realistic values for the response times ($τ_0 \simeq 10^{-10}$ s). Deviations from the bulk anisotropy values found for the smallest particles could be qualitatively explained based on Zener\'{}s relation between $K_1(T)$ and M(T).
△ Less
Submitted 9 July, 2015;
originally announced July 2015.
-
Cell bystander effect induced by radiofrequency electromagnetic fields and magnetic nanoparticles
Authors:
G. F. Goya,
L. Asin,
M. P. Calatayud,
A. Tres,
M. R. Ibarra
Abstract:
Induced effects by direct exposure to ionizing radiation (IR) are a central issue in many fields like radiation protection, clinic diagnosis and oncological therapies. Direct irradiation at certain doses induce cell death, but similar effects can also occur in cells no directly exposed to IR, a mechanism known as bystander effect. Non-IR (radiofrequency waves) can induce the death of cells loaded…
▽ More
Induced effects by direct exposure to ionizing radiation (IR) are a central issue in many fields like radiation protection, clinic diagnosis and oncological therapies. Direct irradiation at certain doses induce cell death, but similar effects can also occur in cells no directly exposed to IR, a mechanism known as bystander effect. Non-IR (radiofrequency waves) can induce the death of cells loaded with MNPs in a focused oncological therapy known as magnetic hyperthermia. Indirect mechanisms are also able to induce the death of unloaded MNPs cells. Using in vitro cell models, we found that colocalization of the MNPs at the lysosomes and the non-increase of the temperature induces bystander effect under non-IR. Our results provide a landscape in which bystander effects are a more general mechanism, up to now only observed and clinically used in the field of radiotherapy.
△ Less
Submitted 3 June, 2015;
originally announced June 2015.
-
Observation of huge thermal spin currents in magnetic multilayers
Authors:
R. Ramos,
T. Kikkawa,
M. H. Aguirre,
I. Lucas,
A. Anadón,
T. Oyake,
K. Uchida,
H. Adachi,
J. Shiomi,
P. A. Algarabel,
L. Morellón,
S. Maekawa,
E. Saitoh,
M. R. Ibarra
Abstract:
Thermal spin pumping constitutes a novel mechanism for generation of spin currents; however their weak intensity constitutes a major roadblock for its usefulness. We report a phenomenon that produces a huge spin current in the central region of a multilayer system, resulting in a giant spin Seebeck effect in a structure formed by repetition of ferromagnet/metal bilayers. The result is a consequenc…
▽ More
Thermal spin pumping constitutes a novel mechanism for generation of spin currents; however their weak intensity constitutes a major roadblock for its usefulness. We report a phenomenon that produces a huge spin current in the central region of a multilayer system, resulting in a giant spin Seebeck effect in a structure formed by repetition of ferromagnet/metal bilayers. The result is a consequence of the interconversion of magnon and electron spin currents at the multiple interfaces. This work opens the possibility to design thin film heterostructures that may boost the application of thermal spin currents in spintronics.
△ Less
Submitted 18 March, 2015;
originally announced March 2015.
-
Enhancement of long range correlations in a 2D vortex lattice by incommensurate 1D disorder potential
Authors:
I. Guillamon,
R. Cordoba,
J. Sese,
J. M. De Teresa,
M. R. Ibarra,
S. Vieira,
H. Suderow
Abstract:
Long range correlations in two-dimensional (2D) systems are significantly altered by disorder potentials. Theory has predicted the existence of disorder induced phenomena such as Anderson localization and the emergence of novel glass and insulating phases as the Bose glass. More recently, it has been shown that disorder breaking the 2D continuous symmetry, such as a one dimensional (1D) modulation…
▽ More
Long range correlations in two-dimensional (2D) systems are significantly altered by disorder potentials. Theory has predicted the existence of disorder induced phenomena such as Anderson localization and the emergence of novel glass and insulating phases as the Bose glass. More recently, it has been shown that disorder breaking the 2D continuous symmetry, such as a one dimensional (1D) modulation, can enhance long range correlations. Experimentally, developments in quantum gases have allowed the observation of a wealth of phenomena induced by the competition between interaction and disorder. However, there are no experiments exploring the effect of symmetry-breaking disorder. Here, we create a 2D vortex lattice at 0.1 K in a superconducting thin film with a well-defined 1D thickness modulation and track the field induced modification using scanning tunneling microscopy. We find that the 1D modulation becomes incommensurate to the vortex lattice and drives an order-disorder transition, behaving as a scale-invariant disorder potential. We show that the transition occurs in two steps and is mediated by the proliferation of topological defects. We find that critical exponents determining the loss of positional and orientational order are far above theoretical expectations for scale-invariant disorder and follow instead the critical behaviour which describes dislocation unbinding melting. Our data show for the first time that randomness disorders a 2D crystal, and evidence enhanced long range correlations in presence of a 1D modulation demonstrating the transformation induced by symmetry breaking disorder in interactions and the critical behaviour of the transition.
△ Less
Submitted 28 October, 2014;
originally announced October 2014.
-
Origin of inverse Rashba-Edelstein effect at Cu/Bi interface using lateral spin valves
Authors:
M. Isasa,
M. C. Martínez-Velarte,
E. Villamor,
C. Magén,
L. Morellón,
J. M. De Teresa,
M. R. Ibarra,
G. Vignale,
E. V. Chulkov,
E. E. Krasovskii,
L. E. Hueso,
F. Casanova
Abstract:
The spin transport and spin-to-charge current conversion properties of bismuth are investigated using permalloy/copper/bismuth (Py/Cu/Bi)lateral spin valve structures. The spin current is strongly absorbed at the surface of Bi, leading to ultra-short spin diffusion lengths. A spin-to-charge current conversion is measured, which is attributed to the inverse Rashba-Edelstein effect at the Cu/Bi inte…
▽ More
The spin transport and spin-to-charge current conversion properties of bismuth are investigated using permalloy/copper/bismuth (Py/Cu/Bi)lateral spin valve structures. The spin current is strongly absorbed at the surface of Bi, leading to ultra-short spin diffusion lengths. A spin-to-charge current conversion is measured, which is attributed to the inverse Rashba-Edelstein effect at the Cu/Bi interface. The spin-current-induced charge current is found to change direction with increasing temperature. A theoretical analysis relates this behavior to the complex spin structure and dispersion of the surface states at the Fermi energy. The understanding of this phenomenon opens novel possibilities to exploit spin-orbit coupling to create, manipulate, and detect spin currents in 2D systems.
△ Less
Submitted 25 December, 2015; v1 submitted 30 September, 2014;
originally announced September 2014.
-
Protein adsorption onto Fe3O4 nanoparticles with opposite surface charge and its impact on cell uptake
Authors:
M. P. Catalayud,
B. Sanz,
V. Raffa,
C. Riggio,
M. R. Ibarra,
G. F. Goya
Abstract:
Nanoparticles (NPs) engineered for biomedical applications are meant to be in contact with protein-rich physiological fluids. These proteins are usually adsorbed onto the NP surface, forming a swaddling layer called protein corona that influences cell internalization. We present a study on protein adsorption onto different magnetic NPs (MNPs) when immersed in cell culture medium, and how these cha…
▽ More
Nanoparticles (NPs) engineered for biomedical applications are meant to be in contact with protein-rich physiological fluids. These proteins are usually adsorbed onto the NP surface, forming a swaddling layer called protein corona that influences cell internalization. We present a study on protein adsorption onto different magnetic NPs (MNPs) when immersed in cell culture medium, and how these changes affect the cellular uptake. Two colloids with magnetite cores of 25 nm, same hydrodynamic size and opposite surface charge were in situ coated with (a) positive polyethyleneimine (PEI-MNPs) and (b) negative poly(acrylic acid) (PAA-MNPs). After few minutes of incubation in cell culture medium the wrapping of the MNPs by protein adsorption resulted in a 5-fold size increase. After 24 h of incubation large MNP-protein aggregates with hydrodynamic sizes 1500 to 3000 nm (PAA-MNPs and PEI-MNPs respectively) were observed. Each cluster contained an estimated number of magnetic cores between 450 and 1000, indicating the formation of large aggregates with a "plum pudding" structure of MNPs embedded into a protein network of negative surface charge irrespective of the MNP_core charge. We demonstrated that PEI-MNPs are incorporated in much larger amounts than the PAA-MNPs units. Quantitative analysis showed that SH-SY5Y cells can incorporate 100 per cent of the added PEI-MNPs up to about 100 pg per cell, whereas for PAA-MNPs the uptake was less than 50 percent. The final cellular distribution showed also notable differences regarding partial attachment to the cell membrane. These results highlight the need to characterize the final properties of MNPs after protein adsorption in biological media, and demonstrate the impact of these properties on the internalization mechanisms in neural cells.
△ Less
Submitted 24 March, 2014; v1 submitted 16 March, 2014;
originally announced March 2014.
-
Magnetic Hyperthermia with Fe3O4 nanoparticles: the Influence of Particle Size on Energy Absorption
Authors:
Gerardo F. Goya,
Enio Lima, Jr.,
Amanda D. Arelaro,
Teobaldo E. Torres,
Hercilio R. Rechenberg,
Liane Rossi,
Clara Marquina,
M. Ricardo Ibarra
Abstract:
We have studied the magnetic and power absorption properties of a series of magnetic nanoparticles (MNPs) of Fe3O4 with average sizes <d> ranging from 3 to 26 nm. Heating experiments as a function of particle size revealed a strong increase in the specific power absorption (SPA) values for particles with <d> = 25-30 nm. On the other side saturation magnetization MS values of these MNPs remain esse…
▽ More
We have studied the magnetic and power absorption properties of a series of magnetic nanoparticles (MNPs) of Fe3O4 with average sizes <d> ranging from 3 to 26 nm. Heating experiments as a function of particle size revealed a strong increase in the specific power absorption (SPA) values for particles with <d> = 25-30 nm. On the other side saturation magnetization MS values of these MNPs remain essentially constant for particles with <d> above 10 nm, suggesting that the absorption mechanism is not determined by MS. The largest SPA value obtained was 130 W/g, corresponding to a bimodal particle distribution with average size values of 17 and 26 nm.
△ Less
Submitted 27 February, 2013;
originally announced February 2013.
-
Observation of the spin Seebeck effect in epitaxial Fe3O4 thin films
Authors:
R. Ramos,
T. Kikkawa,
K. Uchida,
H. Adachi,
I. Lucas,
M. H. Aguirre,
P. Algarabel,
L. Morellon,
S. Maekawa,
E. Saitoh,
M. R. Ibarra
Abstract:
We report the first experimental observation of the spin Seebeck effect in magnetite thin films. The signal observed at temperatures above the Verwey transition is a contribution from both the anomalous Nernst (ANE) and spin Seebeck effects (SSE). The contribution from the ANE of the Fe3O4 layer to the SSE is found to be negligible due to the resistivity difference between Fe3O4 and Pt layers. Bel…
▽ More
We report the first experimental observation of the spin Seebeck effect in magnetite thin films. The signal observed at temperatures above the Verwey transition is a contribution from both the anomalous Nernst (ANE) and spin Seebeck effects (SSE). The contribution from the ANE of the Fe3O4 layer to the SSE is found to be negligible due to the resistivity difference between Fe3O4 and Pt layers. Below the Verwey transition the SSE is free from the ANE of the ferromagnetic layer and it is also found to dominate over the ANE due to magnetic proximity effect on the Pt layer.
△ Less
Submitted 13 December, 2012;
originally announced December 2012.
-
Application of magnetically induced hyperthermia on the model protozoan Crithidia fasciculata as a potential therapy against parasitic infections
Authors:
V. Grazú,
A. M. Silber,
M. Moros,
L. Asín,
T. E. Torres,
C. Marquina,
M. R. Ibarra,
G. F. Goya
Abstract:
Magnetic hyperthermia is currently an EU-approved clinical therapy against tumor cells that uses magnetic nanoparticles under a time varying magnetic field (TVMF). The same basic principle seems promising against trypanosomatids causing Chagas disease and sleeping sickness, since therapeutic drugs available display severe side effects and drug-resistant strains. However, no applications of this st…
▽ More
Magnetic hyperthermia is currently an EU-approved clinical therapy against tumor cells that uses magnetic nanoparticles under a time varying magnetic field (TVMF). The same basic principle seems promising against trypanosomatids causing Chagas disease and sleeping sickness, since therapeutic drugs available display severe side effects and drug-resistant strains. However, no applications of this strategy against protozoan-induced diseases have been reported so far. In the present study, Crithidia fasciculata, a widely used model for therapeutic strategies against pathogenic trypanosomatids, was targeted with Fe_{3}O_{4} magnetic nanoparticles (MNPs) in order to remotely provoke cell death using TVMFs. The MNPs with average sizes of d approx. 30 nm were synthesized using a precipitation of FeSO_{4}4 in basic medium. The MNPs were added to Crithidia fasciculata choanomastigotes in exponential phase and incubated overnight. The amount of uploaded MNPs per cell was determined by magnetic measurements. Cell viability using the MTT colorimetric assay and flow cytometry showed that the MNPs were incorporated by the cells with no noticeable cell-toxicity effects. When a TVMF (f = 249 kHz, H = 13 kA/m) was applied to MNP-bearing cells, massive cell death was induced via a non-apoptotic mechanism. No effects were observed by applying a TVMF on control (without loaded MNPs) cells. No macroscopic rise in temperature was observed in the extracellular medium during the experiments. Scanning Electron Microscopy showed morphological changes after TVMF experiments. These data indicate (as a proof of principle) that intracellular hyperthermia is a suitable technology to induce the specific death of protozoan parasites bearing MNPs. These findings expand the possibilities for new therapeutic strategies that combat parasitic infections.
△ Less
Submitted 1 November, 2012;
originally announced November 2012.
-
Novel multifunctional 90Y-labelled albumin magnetic microspheres for cancer therapy
Authors:
S. Vranješ-\Djurić,
M. Radović,
N. Nikolić,
D. Janković,
G. F. Goya,
T. E. Torres,
M. P. Calatayud,
I. J. Bruvera,
M. R. Ibarra,
V. Spasojević,
B. Jancar,
B. Antić
Abstract:
We present in vitro and in vivo studies of yttrium-90 (90Y)-labelled human serum albumin magnetic microspheres (HSAMMS) as multifunctional agent for bimodal radionuclide-hyperthermia cancer therapy. The HSAMMS were produced using a modified emulsification-heat stabilization technique and contained 10-nm magnetite nanoparticles coated with citric acid, distributed as inhomogeneous clusters within t…
▽ More
We present in vitro and in vivo studies of yttrium-90 (90Y)-labelled human serum albumin magnetic microspheres (HSAMMS) as multifunctional agent for bimodal radionuclide-hyperthermia cancer therapy. The HSAMMS were produced using a modified emulsification-heat stabilization technique and contained 10-nm magnetite nanoparticles coated with citric acid, distributed as inhomogeneous clusters within the albumin microspheres. The average particle size of the complete HSAMMS was 20 (mu)m, and they exhibited superparamagnetic behavior at room temperature. The stability of the 90^Y-labelled HSAMMS was investigated in vitro (in saline and human serum) and in vivo by analyzing their biodistribution in normal Wistar rats. The in vitro experiments revealed the high stability of the labelled HSAMMS in saline and human serum after 72 h. Following the intravenous administration of the 90^Y-HSAMMS in rats, 88.81% of the activity localizes in the lungs after 1 h, with 82.67% remaining after 72 h. These data on 90Y-HSAMMS provide good evidence for their potential use in bimodal radionuclide-hyperthermia cancer therapy.
△ Less
Submitted 11 May, 2012;
originally announced May 2012.
-
Magnetic hydrogels derived from polysaccharides with improved specific power absorption: potential devices for remotely triggered drug delivery
Authors:
R. Hernandez,
J. Sacristan,
L. Asin,
T. E. Torres,
M. R. Ibarra,
G. F. Goya,
C. Mijangos
Abstract:
We report on novel ferrogels derived from polysaccharides (sodium alginate and chitosan) with embedded iron oxide nanoparticles synthesized in situ and their combination with thermally responsive poly (N-isopropylacrylamide) for externally-driven drug release using AC magnetic fields. Samples were characterized by Raman spectroscopy, transmission electron microscopy (TEM) and magnetic measurements…
▽ More
We report on novel ferrogels derived from polysaccharides (sodium alginate and chitosan) with embedded iron oxide nanoparticles synthesized in situ and their combination with thermally responsive poly (N-isopropylacrylamide) for externally-driven drug release using AC magnetic fields. Samples were characterized by Raman spectroscopy, transmission electron microscopy (TEM) and magnetic measurements. The obtained nanoparticles were found to be of ca. 10 nm average size, showing magnetic properties very close to those of the bulk material. The thermal response was measured by power absorption experiments, finding specific power absorption (SPA) values between 100-300 W/g, which was enough for attaining the lower critical solution temperature (LCST) of the polymeric matrix within few minutes. This fast response makes these materials good candidates for externally controlled drug release.
△ Less
Submitted 30 April, 2011;
originally announced May 2011.
-
Magnetic properties and energy absorption of CoFe2O4 nanoparticles for magnetic hyperthermia
Authors:
T. E. Torres,
A. G. Roca,
M. P. Morales,
A. Ibarra,
C. Marquina,
M. R. Ibarra,
G. F. Goya
Abstract:
We have studied the magnetic and power absorption properties of three samples of CoFe2O4 nanoparticles with sizes from 5 to 12 nm prepared by thermal decomposition of Fe (acac)3 and Co(acac)2 at high temperatures. The blocking temperatures TB estimated from magnetization M(T) curves spanned the range 180 < TB < 320 K, reflecting the large magnetocrystalline anisotropy of these nanoparticles. Accor…
▽ More
We have studied the magnetic and power absorption properties of three samples of CoFe2O4 nanoparticles with sizes from 5 to 12 nm prepared by thermal decomposition of Fe (acac)3 and Co(acac)2 at high temperatures. The blocking temperatures TB estimated from magnetization M(T) curves spanned the range 180 < TB < 320 K, reflecting the large magnetocrystalline anisotropy of these nanoparticles. Accordingly, high coercive fields HC \approx 1.4 - 1.7 T were observed at low temperatures. Specific Power Absorption (SPA) experiments carried out in ac magnetic fields indicated that, besides particle volume, the effective magnetic anisotropy is a key parameter determining the absorption efficiency. SPA values as high as 98 W/g were obtained for nanoparticles with average size of \approx12 nm.
△ Less
Submitted 19 March, 2011;
originally announced March 2011.
-
Direct observation of stress accumulation and relaxation in small bundles of superconducting vortices in tungsten thin-films
Authors:
I. Guillamon,
H. Suderow,
S. Vieira,
J. Sese,
R. Cordoba,
J. M. De Teresa,
M. R. Ibarra
Abstract:
We study the behavior of bundles of superconducting vortices when increasing the magnetic field using scanning tunneling microscopy and spectroscopy (STM/S) at 100 mK. Pinning centers are given by features on the surface corrugation. We find strong net vortex motion in a bundle towards a well defined direction. We observe continuos changes of the vortex arrangements, and identify small displacemen…
▽ More
We study the behavior of bundles of superconducting vortices when increasing the magnetic field using scanning tunneling microscopy and spectroscopy (STM/S) at 100 mK. Pinning centers are given by features on the surface corrugation. We find strong net vortex motion in a bundle towards a well defined direction. We observe continuos changes of the vortex arrangements, and identify small displacements, which stress and deform the vortex bundle, separated by larger re-arrangements or avalanches, which release accumulated stress.
△ Less
Submitted 12 January, 2011;
originally announced January 2011.
-
Cell death induced by the application of alternating magnetic fields to nanoparticle-loaded dendritic cells
Authors:
I. Marcos-Campos,
L. Asín,
T. E. Torres,
C. Marquina,
A. Tres,
M. R. Ibarra,
G. F. Goya
Abstract:
In this work, the capability of primary, monocyte-derived dendritic cells (DCs) to uptake iron oxide magnetic nanoparticles (MNPs) is assessed and a strategy to induce selective cell death in these MNP-loaded DCs using external alternating magnetic fields (AMFs) is reported. No significant decrease in the cell viability of MNP-loaded DCs, compared to the control samples, was observed after five da…
▽ More
In this work, the capability of primary, monocyte-derived dendritic cells (DCs) to uptake iron oxide magnetic nanoparticles (MNPs) is assessed and a strategy to induce selective cell death in these MNP-loaded DCs using external alternating magnetic fields (AMFs) is reported. No significant decrease in the cell viability of MNP-loaded DCs, compared to the control samples, was observed after five days of culture. The amount of MNPs incorporated into the cytoplasm was measured by magnetometry, which confirmed that 1 to 5 pg of the particles were uploaded per cell. The intracellular distribution of these MNPs, assessed by transmission electron microscopy, was found to be primarily inside the endosomic structures. These cells were then subjected to an AMF for 30 min, and the viability of the blank DCs (i.e., without MNPs), which were used as control samples, remained essentially unaffected. However, a remarkable decrease of viability from approximately 90% to 2-5% of DCs previously loaded with MNPs was observed after the same 30 min exposure to an AMF. The same results were obtained using MNPs having either positive (NH2+) or negative (COOH-) surface functional groups. In spite of the massive cell death induced by application of AMF to MNP-loaded DCs, the amount of incorporated magnetic particles did not raise the temperature of the cell culture. Clear morphological changes at the cell structure after magnetic field application were observed using scanning electron microscopy. Therefore, local damage produced by the MNPs could be the main mechanism for the selective cell death of MNP-loaded DCs under an AMF. Based on the ability of these cells to evade the reticuloendothelial system, these complexes combined with an AMF should be considered as a potentially powerful tool for tumour therapy.
△ Less
Submitted 19 March, 2011; v1 submitted 5 September, 2010;
originally announced September 2010.
-
Direct observation of melting in a 2-D superconducting vortex lattice
Authors:
I. Guillamon,
H. Suderow,
A. Fernandez-Pacheco,
J. Sese,
R. Cordoba,
J. M. De Teresa,
M. R. Ibarra,
S. Vieira
Abstract:
Topological defects such as dislocations and disclinations are predicted to determine the twodimensional (2-D) melting transition. In 2-D superconducting vortex lattices, macroscopic measurements evidence melting close to the transition to the normal state. However, the direct observation at the scale of individual vortices of the melting sequence has never been performed. Here we provide step b…
▽ More
Topological defects such as dislocations and disclinations are predicted to determine the twodimensional (2-D) melting transition. In 2-D superconducting vortex lattices, macroscopic measurements evidence melting close to the transition to the normal state. However, the direct observation at the scale of individual vortices of the melting sequence has never been performed. Here we provide step by step imaging through scanning tunneling spectroscopy of a 2-D system of vortices up to the melting transition in a focused-ion-beam nanodeposited W-based superconducting thin film. We show directly the transition into an isotropic liquid below the superconducting critical temperature. Before that, we find a hexatic phase, characterized by the appearance of free dislocations, and a smectic-like phase, possibly originated through partial disclination unbinding. These results represent a significant step in the understanding of melting of 2-D systems, with impact across several research fields, such as liquid crystal molecules, or lipids in membranes.
△ Less
Submitted 14 August, 2009;
originally announced August 2009.
-
Superconducting density of states at the border of an amorphous thin film grown by focused-ion-beam
Authors:
I. Guillamon,
H. Suderow,
S. Vieira,
A. Fernandez-Pacheco,
J. Sese,
R. Cordoba,
J. M. De Teresa,
M. R. Ibarra
Abstract:
We present very low temperature Scanning Tunneling Microscopy and Spectroscopy (STM/S) measurements of a W based amorphous thin film grown with focused-ion-beam. In particular, we address the superconducting properties close to the border, where the thickness of the superconducting film decreases, and the Au substrate emerges. When approaching the Au substrate, the superconducting tunneling cond…
▽ More
We present very low temperature Scanning Tunneling Microscopy and Spectroscopy (STM/S) measurements of a W based amorphous thin film grown with focused-ion-beam. In particular, we address the superconducting properties close to the border, where the thickness of the superconducting film decreases, and the Au substrate emerges. When approaching the Au substrate, the superconducting tunneling conductance strongly increases around the Fermi level, and the quasiparticle peaks do not significantly change its position. Under magnetic fields, the vortex lattice is observed, with vortices positioned very close to the Au substrate.
△ Less
Submitted 24 February, 2009;
originally announced February 2009.
-
Magnetic Nanoparticles for Power Absorption: optimizing size, shape and magnetic properties
Authors:
M. A. Gonzalez-Fernandez,
T. Torres,
M. Andres-Verges,
R. Costo,
P. de la Presa,
C. J. Serna,
M. P. Morales,
C. Marquina,
M. R. Ibarra,
G. F. Goya
Abstract:
We present a study on the magnetic properties of naked and silica-coated Fe3O4 nanoparticles with sizes between 5 and 110 nm. Their efficiency as heating agents was assessed through specific power absorption (SPA) measurements as a function of particle size and shape. The results show a strong dependence of the SPA with the particle size, with a maximum around 30 nm, as expected for a Neel relax…
▽ More
We present a study on the magnetic properties of naked and silica-coated Fe3O4 nanoparticles with sizes between 5 and 110 nm. Their efficiency as heating agents was assessed through specific power absorption (SPA) measurements as a function of particle size and shape. The results show a strong dependence of the SPA with the particle size, with a maximum around 30 nm, as expected for a Neel relaxation mechanism in single-domain particles. The SiO2 shell thickness was found to play an important role in the SPA mechanism by hindering the heat outflow, thus decreasing the heating efficiency. It is concluded that a compromise between good heating efficiency and surface functionality for biomedical purposes can be attained by making the SiO2 functional coating as thin as possible.
△ Less
Submitted 25 January, 2009;
originally announced January 2009.
-
Nanoscale superconducting properties of amorphous W-based deposits grown with focused-ion-beam
Authors:
I. Guillamon,
H. Suderow,
S. Vieira,
A. Fernandez-Pacheco,
J. Sese,
R. Cordoba,
J. M. De Teresa,
M. R. Ibarra
Abstract:
We present very low temperature Scanning Tunneling Microscopy and Spectroscopy (STM/S) measurements in W-based amorphous superconducting nanodeposits grown using a metal-organic precursor and focused-ion-beam. The superconducting gap closely follows s-wave BCS theory, and STS images under magnetic fields show a hexagonal vortex lattice whose orientation is related to features observed in the top…
▽ More
We present very low temperature Scanning Tunneling Microscopy and Spectroscopy (STM/S) measurements in W-based amorphous superconducting nanodeposits grown using a metal-organic precursor and focused-ion-beam. The superconducting gap closely follows s-wave BCS theory, and STS images under magnetic fields show a hexagonal vortex lattice whose orientation is related to features observed in the topography through STM. Our results demonstrate that the superconducting properties at the surface of these deposits are very homogeneous, down to atomic scale. This, combined with the huge nanofabrication possibilities of the focused-ion-beam technique, paves the way to use focused-ion-beam to make superconducting circuitry of many different geometries.
△ Less
Submitted 30 May, 2008;
originally announced May 2008.
-
Unusual magnetic behavior in ferrite hollow nanospheres
Authors:
E. Lima Jr,
J. M. Vargas,
R. D. Zysler,
H. R. Rechenberg,
J. Arbiol,
G. F. Goya,
A. Ibarra,
M. R. Ibarra
Abstract:
We report unusual magnetic behavior in iron oxide hollow nanospheres of 9.3 $nm$ in diameter. The large fraction of atoms existing at the inner and outer surfaces gives rise to a high magnetic disorder. The overall magnetic behavior can be explained considering the coexistence of a soft superparamagnetic phase and a hard phase corresponding to the highly frustrated cluster-glass like phase at th…
▽ More
We report unusual magnetic behavior in iron oxide hollow nanospheres of 9.3 $nm$ in diameter. The large fraction of atoms existing at the inner and outer surfaces gives rise to a high magnetic disorder. The overall magnetic behavior can be explained considering the coexistence of a soft superparamagnetic phase and a hard phase corresponding to the highly frustrated cluster-glass like phase at the surface regions.
△ Less
Submitted 21 April, 2008;
originally announced April 2008.
-
Direct evidence of the orbital contribution to the magnetic moment in AA'FeReO6 double perovskites
Authors:
M. Sikora,
D. Zajac,
C. Kapusta,
M. Borowiec,
C. J. Oates,
V. Prochazka,
D. Rybicki,
J. M. De Teresa,
C. Marquina,
M. R. Ibarra
Abstract:
Spin and orbital magnetic moments of Re in AA'FeReO6 double perovskites (A,A' = Ba, Sr, Ca) have been directly probed employing XMCD spectroscopy at the Re L2,3-edges. A considerable orbital magnetic moment is observed in all the studied compounds despite octahedral coordination. Relative orbital to spin contribution per Re atom rises with lattice distortion from mL/mS = -0.28 to -0.34 for AA'=B…
▽ More
Spin and orbital magnetic moments of Re in AA'FeReO6 double perovskites (A,A' = Ba, Sr, Ca) have been directly probed employing XMCD spectroscopy at the Re L2,3-edges. A considerable orbital magnetic moment is observed in all the studied compounds despite octahedral coordination. Relative orbital to spin contribution per Re atom rises with lattice distortion from mL/mS = -0.28 to -0.34 for AA'=Ba2FeReO6 and Ca2FeReO6, respectively. A preliminary XMCD measurements at the Fe L2,3-edges reveals also a significant orbital moment of iron in Ca2FeReO6. The relation of the results to the magnetic properties of the compounds is discussed.
△ Less
Submitted 15 March, 2005;
originally announced March 2005.
-
Huge Ballistic Magnetoresistance in Multiple Nanocontacts Devices
Authors:
N. Garcia,
M. R. Ibarra,
C. Hao1,
R. F. Pacheco,
D. Serrate
Abstract:
In this paper we report an exhaustive experimental work on magnetoresistance effects found in a system in which a large number of nanocontacts are produced between oxidized Fe fine particles. We have obtained the following performances: i) Huge low field room temperature magnetoresistance (over 1000%). ii) Non-linear I-V at different applied fields and temperatures. iii) Large thermal stability…
▽ More
In this paper we report an exhaustive experimental work on magnetoresistance effects found in a system in which a large number of nanocontacts are produced between oxidized Fe fine particles. We have obtained the following performances: i) Huge low field room temperature magnetoresistance (over 1000%). ii) Non-linear I-V at different applied fields and temperatures. iii) Large thermal stability and reproducible resistance value under thermal cycles from room temperature down to 5 K. iv) Easy to fabricate with an almost 100% success. v) Heavy duty and transportable samples with reproducibility tested in several laboratories. We realized that the extraordinary effect found is related to the oxygen content at the particles surface
△ Less
Submitted 2 February, 2005;
originally announced February 2005.
-
Large positive magnetocaloric effect in a perovskite manganite
Authors:
R. Mahendiran,
B. G. Ueland,
P. Schiffer,
A. Maignan,
C. Martin,
M. Hervieu,
B. Raveau,
M. R. Ibarra,
L. Morellon
Abstract:
We investigate the magnetothermodynamic properties of the perovskite manganite Pr0.46Sr0.54MnO3. Our data imply that the paramagnetic to antiferromagnetic transition at TN = 210 K is first order with an abrupt decrease of volume (~ 0.14 % in zero magnetic field) and is accompanied by a sharp anomaly in specific heat. Upon application of a sufficiently large magnetic field, the antiferromagnetic…
▽ More
We investigate the magnetothermodynamic properties of the perovskite manganite Pr0.46Sr0.54MnO3. Our data imply that the paramagnetic to antiferromagnetic transition at TN = 210 K is first order with an abrupt decrease of volume (~ 0.14 % in zero magnetic field) and is accompanied by a sharp anomaly in specific heat. Upon application of a sufficiently large magnetic field, the antiferromagnetic phase transforms into a ferromagnetic phase with a sharp increase in sample volume. This field induced transition results in a large positive magnetocaloric effect just below TN (∆Sm = 10.4 Jkg-1K-1 at H = 5.5 T), which is associated with the increasing stability of the antiferromagnetic state with decreasing temperature.
△ Less
Submitted 9 June, 2003;
originally announced June 2003.
-
Field-induced magnetic anisotropy in La0.7Sr0.3CoO3
Authors:
J. Mira,
J. Rivas,
M. Vazquez,
M. R. Ibarra,
R. Caciuffo,
M. A. Senaris Rodriguez
Abstract:
Magnetic anisotropy has been measured for the ferromagnetic La0.7Sr0.3CoO3 perovskite from an analysis of the high-field part of the magnetization vs. field curves, i.e., the magnetic saturation regime. These measurements give a magnetic anistropy one order of magnitude higher than that of reference manganites. Surprisingly, the values of the magnetic anisotropy calculated in this way do not coi…
▽ More
Magnetic anisotropy has been measured for the ferromagnetic La0.7Sr0.3CoO3 perovskite from an analysis of the high-field part of the magnetization vs. field curves, i.e., the magnetic saturation regime. These measurements give a magnetic anistropy one order of magnitude higher than that of reference manganites. Surprisingly, the values of the magnetic anisotropy calculated in this way do not coincide with those estimated from measurements of coercive fields which are one order of magnitude smaller. It is proposed that the reason of this anomalous behaviour is a transition of the trivalent Co ions under the external magnetic field from a low-spin to an intermediate-spin state. Such a transition converts the Co3+ ions into Jahn-Teller ions having an only partially quenched orbital angular momentum, which enhances the intra-atomic spin-orbit coupling and magnetic anisotropy.
△ Less
Submitted 9 April, 2003;
originally announced April 2003.
-
Giant anisotropic magnetostriction in Pr$_{0.5}$Sr$_{0.5}$MnO$_3$
Authors:
R. Mahendiran,
C. Marquina,
M. R. Ibarra,
A. Arulraj,
C. N. R. Rao,
A. Maignan,
B. Raveau
Abstract:
Magnetic, linear thermal expansion (LTE), anisotropic ($λ_t$) and volume ($ω$) magnetostriction properties of Pr$_{0.5}$Sr$_{0.5}$MnO$_3$ were investigated. The LTE decreases smoothly from 300 K without a clear anomaly either around the Curie (T$_C$ = 270 K) or the Neel temperature (T$_N$ = 100 K) and it exhibits hysteresis over a wide temperature range (60 K-270 K) upon warming. Isothermal magn…
▽ More
Magnetic, linear thermal expansion (LTE), anisotropic ($λ_t$) and volume ($ω$) magnetostriction properties of Pr$_{0.5}$Sr$_{0.5}$MnO$_3$ were investigated. The LTE decreases smoothly from 300 K without a clear anomaly either around the Curie (T$_C$ = 270 K) or the Neel temperature (T$_N$ = 100 K) and it exhibits hysteresis over a wide temperature range (60 K-270 K) upon warming. Isothermal magnetization study suggests that 13 % of the ferromagnetic phase coexists with 87 % of the antiferromagnetic phase at 25 K. The parallel and perpendicular magnetostrictions undergo rapid changes during the metamagnetic transition. Contrary to the isotropic giant volume magnetostriction reported in manganites so far, this compound exhibits a giant anisotropic magnetostriction ($λ_t \approx 10^{-3}$) and smaller volume ($ω\approx 10^{-4}$) magnetostrictions below T$_N$. We suggest that the field induced antiferromagnetic to ferromagnetic transition is accompanied by a structural transition from the d$_{x^2-y^2}$ orbital ordered antiferromagnetic (orthorhombic) to the orbital disordered ferromagnetic (tetragonal) phase. The metamagnetic transition proceeds through nucleation and growth of the ferromagnetic domains at the expense of the antiferromagnetic phase. The preferential orientation of the ferromagnetic (tetragonal) domains along the field direction increases the linear dimension of the sample in the field direction and decreases in the orthogonal direction leading to the observed giant anisotropic magnetostriction effect. Our study also suggests that nanodomains of the low temperature antiferromagnetic phase possibly exist in the temperature region T$_N$ < T < T$_C$.
△ Less
Submitted 9 August, 2001; v1 submitted 3 August, 2001;
originally announced August 2001.
-
Lattice coupled first order magnetoresistance transition in an A-type antiferromagnet: Pr$_{0.46}$Sr$_{0.54}$MnO$_3$
Authors:
R. Mahendiran,
C. Martin,
A. Maignan,
M. Hervieu,
B. Raveau,
L. Morellon,
C. Marquina,
B. Garcia-Landa,
M. R. Ibarra
Abstract:
We investigated magnetic, magnetotransport and magnetostriction properties of the A-type antiferromagnet Pr$_{0.46}$Sr$_{0.54}$MnO$_3$ which undergoes a first order paramagnetic-antiferromagnetic transition below T$_N$ = 210 K while cooling and T$_N$ = 215 K while warming. The zero field ($μ_0$H = 0 T) resistivity shows a sudden jump at T$_N$ and a small bump around T$_{max}$ = 220 K (\TEXTsymbo…
▽ More
We investigated magnetic, magnetotransport and magnetostriction properties of the A-type antiferromagnet Pr$_{0.46}$Sr$_{0.54}$MnO$_3$ which undergoes a first order paramagnetic-antiferromagnetic transition below T$_N$ = 210 K while cooling and T$_N$ = 215 K while warming. The zero field ($μ_0$H = 0 T) resistivity shows a sudden jump at T$_N$ and a small bump around T$_{max}$ = 220 K (\TEXTsymbol{>} T$_N$). T$_N$ shifts down and T$_{max}$ shifts up with increasing $μ_0$H. Magnetoresistance as high as -45-57 % at 7 T is found in the temperature range 180 K-230 K. Isothermal measurements indicate that the field induced antiferromagnetic to ferromagnetic transition below T$_N$ is accompanied by a rapid decrease of the resistivity but increase of volume ($Δ$V/V = +0.25 % at 180 K and 13.7 T). This lattice coupled magnetoresistance transition is suggested due to the field induced structural transition from the low volume orthorhombic to the high volume tetragonal structure.
△ Less
Submitted 26 July, 2001;
originally announced July 2001.
-
Magnetic-field -induced structural changes in the electron doped manganites: CaxSm1-xMnO3 (x = 0.8, 0.85)
Authors:
R. Mahendiran,
P. A. Algarabel,
L. Morellon,
C. Marquina,
M. R. Ibarra,
A. Maignan,
C. Martin,
M. Hervieu,
B. Raveau,
C. Ritter
Abstract:
We studied the correlation between magnetic, electrical, structural, and magnetostriction properties of the electron doped manganites Ca$_x$Sm$_{1-x}$MnO$_3$ (x = 0.85, 0.8). The paramagnetic to antiferromagnetic transition in both the compounds while cooling is accompanied by an abrupt increase of the spontaneous volume thermal expansion ($Δ$V/V = 0.07 % for x = 0.85 and 0.25 % for x = 0.2). Th…
▽ More
We studied the correlation between magnetic, electrical, structural, and magnetostriction properties of the electron doped manganites Ca$_x$Sm$_{1-x}$MnO$_3$ (x = 0.85, 0.8). The paramagnetic to antiferromagnetic transition in both the compounds while cooling is accompanied by an abrupt increase of the spontaneous volume thermal expansion ($Δ$V/V = 0.07 % for x = 0.85 and 0.25 % for x = 0.2). The x = 0.15 exhibits multiple phase separation at 5 K: G-type, and C-type antiferromagnetic phases in orthorhombic (\QTR{it}{Pnma}) and monoclinic (\QTR{it}{P2}$_1$\QTR{it}{/m}) structures respectively. Magnetic study on x = 0.85 also suggest ferromagnetic regions possibly in $Pnma$ structure coexist with the antiferromagnetic phases. The magnetization (M = 1.2 $μ_B$) of x = 0.85 does not reach the value expected for the complete alignment of Mn spins even at 12 T and at 12 K. Metamagnetic transitions (C-type to Ferromagnetic) in both compounds are accompanied by contraction of volumes under high magnetic fields. We suggest that a high magnetic field induces \QTR{it}{P2}$_1$\QTR{it}{/m} (high volume) to \QTR{it}{Pnma} (low volume) structural transition. This is also supported by the neutron diffraction study.
△ Less
Submitted 8 June, 2001;
originally announced June 2001.