Strengthening of Mg-Al-Ca alloys with C15 and C36 Laves phases
Authors:
Mhammad Zubair,
Stefanie Sandlöbes-Haut,
Risheng Pei,
Maximilian A. Wollenweber,
James S. K-L. Gibson,
S. Korte-Kerzel
Abstract:
The Laves phase skeleton in cast Mg-Al-Ca alloys is known to provide considerable strengthening. Laves phases such as CaMg$_2$ (C14), Ca(Al,Mg)$_2$ (C36), and CaAl2 (C15) have high melting points, high hardness at room and elevated temperatures, but unfortunately are inherently brittle. Mg-Al-Ca alloys thus have good creep properties but limited ductility. An understanding of the co-deformation be…
▽ More
The Laves phase skeleton in cast Mg-Al-Ca alloys is known to provide considerable strengthening. Laves phases such as CaMg$_2$ (C14), Ca(Al,Mg)$_2$ (C36), and CaAl2 (C15) have high melting points, high hardness at room and elevated temperatures, but unfortunately are inherently brittle. Mg-Al-Ca alloys thus have good creep properties but limited ductility. An understanding of the co-deformation behaviour of $α$-Mg and Laves phases is essential for optimising the strength-ductility balance of these alloys. Here, we study the mechanical behaviour of a Mg-4.65Al-2.82Ca alloy using micropillar compression in the $α$-Mg matrix, at $α$-Mg/C36 and $α$-Mg/C15 interfaces and in the C15 phase in combination with scanning electron microscopy (SE imaging), electron backscatter diffraction (EBSD), transmission Kikuchi diffraction (TKD), and low-kV scanning transmission electron microscopy (STEM). We show that both, C15 and C36, Laves phases provide considerable strengthening to the $α$-Mg matrix by delaying the onset of basal slip and extension twinning, while only the C36 phase appears to allow a certain extent of slip transfer/ plastic co-deformation, in spite of its greater anisotropy compared with the cubic C15 phase. We therefore conclude based on these results that strengthening of the $α$-Mg matrix by the C36 Laves phase is preferable given that it combines easy skeleton formation with some co-deformation and considerable stability at common application temperatures of magnesium alloys.
△ Less
Submitted 9 February, 2023;
originally announced February 2023.
-
Plasticity of the Nb-rich μ-Co7Nb6 phase at room temperature and 600 °C
Authors:
W. Luo,
Z. Xie,
P. -L. Sun,
J. S. K. -L. Gibson,
S. Korte-Kerzel
Abstract:
The μ-phase is a common precipitation phase in superalloys and it exists in a wide composition and temperature range. As such, we study the influences of composition and temperature on its plasticity by micropillar compression tests and transmission electron microscopy. The micropillars of the μ-Co7Nb6 phase deform plastically by basal slip at either room temperature or 600 oC. At room temperature…
▽ More
The μ-phase is a common precipitation phase in superalloys and it exists in a wide composition and temperature range. As such, we study the influences of composition and temperature on its plasticity by micropillar compression tests and transmission electron microscopy. The micropillars of the μ-Co7Nb6 phase deform plastically by basal slip at either room temperature or 600 oC. At room temperature, the Co-49Nb and Co-52Nb micropillars show high yield stresses and an abrupt large strain burst at the onset of yielding regardless of orientation, whereas the Co-54Nb micropillars oriented for basal slip yield at much lower stresses and show intermittent small strain bursts during plastic deformation. While the Co-49Nb micropillars deform by full dislocation slip on the basal plane at room temperature, the Co-54Nb micropillars deform by partial dislocation slip on the basal plane. At 600 oC, the Co-49Nb micropillars oriented for basal slip show stable and continuous plasticity and their critical resolved shear stress decreases dramatically. The plastic deformation of the Co-49Nb micropillars occurs via partial dislocation slip on the basal plane at 600 oC. Based on the geometric γ-surfaces for all potential basal slip planes, we explore where and why the glide of full and partial dislocations on the basal plane occurs in the μ-Co7Nb6 phase.
△ Less
Submitted 31 January, 2023; v1 submitted 23 January, 2023;
originally announced January 2023.
-
Plasticity of the Al$_{2}$Cu θ-phase from ambient temperature to 300°C
Authors:
D. Andre,
J. S. K. -L. Gibson,
P. -L. Sun,
N. Lohrey,
S. Sandlöbes-Haut,
S. Korte-Kerzel
Abstract:
The investigation of the deformation behaviour of intermetallic phases is mostly limited to high temperatures due to their low ductility at ambient temperature. Therefore, within this study, nanoindentation experiments on the Al$_{2}$Cu phase were performed from ambient temperature up to 300°C in conjunction with TEM investigations of the deformed material. It was found that the Al$_{2}$Cu phase s…
▽ More
The investigation of the deformation behaviour of intermetallic phases is mostly limited to high temperatures due to their low ductility at ambient temperature. Therefore, within this study, nanoindentation experiments on the Al$_{2}$Cu phase were performed from ambient temperature up to 300°C in conjunction with TEM investigations of the deformed material. It was found that the Al$_{2}$Cu phase starts to soften from temperatures above 150°C. The low temperature deformation behaviour was dominated by serrated yielding and transitioned towards a smooth deformation behaviour above 150°C. No slip traces were observed in the vicinity of the indents in both temperature regimes. The predominant dislocations observed after ambient temperature deformation and elevated temperature deformation are assumed to belong to the same operating slip systems. Therefore, the underlying deformation mechanism for both temperatures appears to be the same and thermally activated.
△ Less
Submitted 13 December, 2021;
originally announced December 2021.
-
Plastic deformation of the CaMg$_{2}$ C14-Laves phase from 50-250$^\circ$C
Authors:
Martina Freund,
Doreen Andre,
Christoffer Zehnder,
Hanno Rempel,
Dennis Gerber,
Muhammad Zubair,
Stefanie Sandlöbes-Haut,
James S. K. -L. Gibson,
Sandra Korte-Kerzel
Abstract:
Intermetallic phases can significantly improve the creep resistance of magnesium alloys, extending their use to higher temperatures. However, little is known about the deformation behaviour of these phases at application temperatures, which are commonly below their macroscopic brittle-to-ductile-transition temperature. In this study, we therefore investigate the activation of different slip system…
▽ More
Intermetallic phases can significantly improve the creep resistance of magnesium alloys, extending their use to higher temperatures. However, little is known about the deformation behaviour of these phases at application temperatures, which are commonly below their macroscopic brittle-to-ductile-transition temperature. In this study, we therefore investigate the activation of different slip systems of the CaMg$_2$ phase and the occurrence of serrated yielding in the temperature range from 50$^\circ$C to 250$^\circ$C. A decreasing amount of serrated flow with increasing temperature suggests that solute atoms govern the flow behaviour when the CaMg$_{2}$ phase is off-stoichiometric.
△ Less
Submitted 23 September, 2021;
originally announced September 2021.
-
Co-deformation Between the Metallic Matrix and Intermetallic Phases in a Creep-Resistant Mg-3.68Al-3.8Ca Alloy
Authors:
M. Zubair,
S. Sandlöbes-Haut,
M. Lipińska-Chwałek,
M. A. Wollenweber,
C. Zehnder,
J. Mayer,
J. S. K-L. Gibson,
S. Korte-Kerzel
Abstract:
The microstructure of Mg-Al-Ca alloys consists of a hard intra- and intergranular eutectic Laves phase network embedded in a soft $α$-Mg matrix. For such heterogeneous microstructures, the mechanical response and co-deformation of both phases under external load are not yet fully understood. We therefore used nano- and microindentation in combination with electron microscopy to study the deformati…
▽ More
The microstructure of Mg-Al-Ca alloys consists of a hard intra- and intergranular eutectic Laves phase network embedded in a soft $α$-Mg matrix. For such heterogeneous microstructures, the mechanical response and co-deformation of both phases under external load are not yet fully understood. We therefore used nano- and microindentation in combination with electron microscopy to study the deformation behaviour of an Mg-3.68Al-3.8Ca alloy.
We found that the hardness of the Mg$_2$Ca phase was significantly larger than the $α$-Mg phase and stays constant within the measured temperature range. The strain rate sensitivity of the softer $α$-Mg phase and of the interfaces increased while activation volume decreased with temperature. The creep deformation of the Mg$_2$Ca Laves phase was significantly lower than the $α$-Mg phase at 170 $^{\circ}$C. Moreover, the deformation zone around and below microindents depends on the matrix orientation and is influenced by the presence of Laves phases. Most importantly, slip transfer from the $α$-Mg phase to the (Mg,Al)$_2$Ca Laves phase occurred, carried by the basal planes. Based on the observed orientation relationship and active slip systems, a slip transfer mechanism from the soft $α$-Mg phase to the hard Laves phase is proposed. Further, we present implications for future alloy design strategies.
△ Less
Submitted 30 August, 2021;
originally announced August 2021.
-
Deformation of micrometer and mm-sized Fe2.4wt.%Si single- and bi-crystals with a high angle grain boundary at room temperature
Authors:
Martin Heller,
James S. K. -L. Gibson,
Risheng Pei,
Sandra Korte-Kerzel
Abstract:
Plasticity in body-centred cubic (BCC) metals, including dislocation interactions at grain boundaries, is much less understood than in face-centred cubic (FCC) metals. At low temperatures additional resistance to dislocation motion due to the Peierls barrier becomes important, which increases the complexity of plasticity. Iron-silicon steel is an interesting, model BCC material since the evolution…
▽ More
Plasticity in body-centred cubic (BCC) metals, including dislocation interactions at grain boundaries, is much less understood than in face-centred cubic (FCC) metals. At low temperatures additional resistance to dislocation motion due to the Peierls barrier becomes important, which increases the complexity of plasticity. Iron-silicon steel is an interesting, model BCC material since the evolution of the dislocation structure in specifically-oriented grains and at particular grain boundaries have far-reaching effects not only on the deformation behaviour but also on the magnetic properties, which are important in its final application as electrical steel. In this study, two different orientations of micropillars (1, 2, 4 microns in diameter) and macropillars (2500 microns) and their corresponding bi crystals are analysed after compression experiments with respect to the effect of size on strength and dislocation structures. Using different experimental methods, such as slip trace analysis, plane tilt analysis and cross-sectional EBSD, we show that direct slip transmission occurs, and different slip systems are active in the bi-crystals compared to their single-crystal counterparts. However, in spite of direct transmission and a very high transmission factor, dislocation pile-up at the grain boundary is also observed at early stages of deformation. Moreover, an effect of size scaling with the pillar size in single crystals and the grain size in bi-crystals is found, which is consistent with investigations elsewhere in FCC metals.
△ Less
Submitted 10 June, 2020; v1 submitted 22 April, 2020;
originally announced April 2020.
-
Low temperature deformation of MoSi$_2$ and the effect of Ta, Nb and Al as alloying elements
Authors:
Carolin Zenk,
James S. K. -L. Gibson,
Verena Maier-Kiener,
Steffen Neumeier,
Mathias Göken,
Sandra Korte-Kerzel
Abstract:
Molybdenum disilicide (MoSi$_2$) is a very promising material for high temperature structural applications due to its high melting point (2030 °C), low density, high thermal conductivity and good oxidation resistance. However, MoSi$_2$ has limited ductility below 900 °C due to its anisotropic plastic deformation behaviour and high critical resolved shear stresses on particular slip systems. Nanoin…
▽ More
Molybdenum disilicide (MoSi$_2$) is a very promising material for high temperature structural applications due to its high melting point (2030 °C), low density, high thermal conductivity and good oxidation resistance. However, MoSi$_2$ has limited ductility below 900 °C due to its anisotropic plastic deformation behaviour and high critical resolved shear stresses on particular slip systems. Nanoindentation of MoSi$_2$ microalloyed with aluminium, niobium or tantalum showed that all alloying elements cause a decrease in hardness. Analysis of surface slip lines indicated the activation of the additional {1 1 0}<1 1 1> slip system in microalloyed MoSi$_2$, which is not active below 300 °C in pure MoSi$_2$. This was confirmed by TEM dislocation analysis of the indentation plastic zone. Further micropillar compression experiments comparing pure MoSi$_2$ and the Ta-alloyed sample enabled the determination of the critical resolved shear stresses of individual slip systems even in the most brittle [0 0 1] crystal direction.
△ Less
Submitted 10 September, 2019;
originally announced September 2019.
-
Mechanical Characterisation of the Protective Al$_2$O$_3$ Scale in Cr$_2$AlC MAX phases
Authors:
J. S. K. -L. Gibson,
J. Gonzalez-Julian,
S. Krishnan,
R. Vaßen,
S. Korte-Kerzel
Abstract:
MAX phases have great potential under demands of both high-temperature and high-stress performance, with their mixed atomic bonding producing the temperature and oxidation resistance of ceramics with the mechanical resilience of metals. Here, we measure the mechanical properties up to 980C by nanoindentation on highly dense and pure Cr$_2$AlC, as well as after oxidation with a burner rig at 1200C…
▽ More
MAX phases have great potential under demands of both high-temperature and high-stress performance, with their mixed atomic bonding producing the temperature and oxidation resistance of ceramics with the mechanical resilience of metals. Here, we measure the mechanical properties up to 980C by nanoindentation on highly dense and pure Cr$_2$AlC, as well as after oxidation with a burner rig at 1200C for more than 29 hours. Only modest reductions in both hardness and modulus up to 980C were observed, implying no change in deformation mechanism. Furthermore, micro-cantilever fracture tests were carried out at the Cr$_2$AlC/Cr$_7$C$_3$ and Cr$_7$C$_3$/Al$_2$O$_3$ interfaces after the oxidation of the Cr$_2$AlC substrates with said burner rig. The values are typical of ceramic-ceramic interfaces, below 4 MPa/m, leading to the hypothesis that the excellent macroscopic behaviour is due to a combination of low internal strain due to the match in thermal expansion coefficient as well as the convoluted interface.
△ Less
Submitted 29 July, 2019;
originally announced July 2019.
-
On Extracting Mechanical Properties from Nanoindentation at Temperatures up to 1000$^{\circ}$C
Authors:
James S. K. -L. Gibson,
Sebastian Schröders,
Christoffer Zehnder,
Sandra Korte-Kerzel
Abstract:
Alloyed MCrAlY bond coats, where M is usually cobalt and/or nickel, are essential parts of modern turbine blades, imparting environmental resistance while mediating thermal expansivity differences. Nanoindentation allows the determination of their properties without the complexities of traditional mechanical tests, but was not previously possible near turbine operating temperatures.
Here, we det…
▽ More
Alloyed MCrAlY bond coats, where M is usually cobalt and/or nickel, are essential parts of modern turbine blades, imparting environmental resistance while mediating thermal expansivity differences. Nanoindentation allows the determination of their properties without the complexities of traditional mechanical tests, but was not previously possible near turbine operating temperatures.
Here, we determine the hardness and modulus of CMSX-4 and an Amdry-386 bond coat by nanoindentation up to 1000$^{\circ}$C. Both materials exhibit a constant hardness until 400$^{\circ}$C followed by considerable softening, which in CMSX-4 is attributed to the multiple slip systems operating underneath a Berkovich indenter.
The creep behaviour has been investigated via the nanoindentation hold segments. Above 700$^{\circ}$C, the observed creep exponents match the temperature-dependence of literature values in CMSX-4. In Amdry-386, nanoindentation produces creep exponents very close to literature data, implying high-temperature nanoindentation may be powerful in characterising these coatings and providing inputs for material, model and process optimisations.
△ Less
Submitted 22 September, 2017;
originally announced September 2017.