Alloying Effects on the Microstructure and Properties of Laser Additively Manufactured Tungsten Materials
Authors:
W. Streit Cunningham,
Eric Lang,
David J. Sprouster,
Nicholas Olynik,
Ajith Pattammattel,
Daniel Olds,
Khalid Hattar,
Ian McCue,
Jason R. Trelewicz
Abstract:
A large body of literature within the additive manufacturing (AM) community has focused on successfully creating stable tungsten (W) microstructures due to significant interest in its application for extreme environments. However, solidification cracking and additional embrittling features at grain boundaries have resulted in poorly performing microstructures, stymying the application of AM as a m…
▽ More
A large body of literature within the additive manufacturing (AM) community has focused on successfully creating stable tungsten (W) microstructures due to significant interest in its application for extreme environments. However, solidification cracking and additional embrittling features at grain boundaries have resulted in poorly performing microstructures, stymying the application of AM as a manufacturing technique for W. Several alloying strategies, such as ceramic particles and ductile elements, have emerged with the promise to eliminate solidification cracking while simultaneously enhancing stability against recrystallization. In this work, we provide new insights regarding the defects and microstructural features that result from the introduction of ZrC for grain refinement and NiFe as a ductile reinforcement phase - in addition to the resulting thermophysical and mechanical properties. ZrC is shown to promote microstructural stability with increased hardness due to the formation of ZrO2 dispersoids. Conversely, NiFe forms into micron-scale FCC phase regions within a BCC W matrix, producing enhanced toughness relative to pure AM W. A combination of these effects is realized in the WNiFe+ZrC system and demonstrates that complex chemical environments coupled with the tuning of AM microstructures provides an effective pathway for enabling laser AM W materials with enhanced stability and performance.
△ Less
Submitted 3 November, 2023;
originally announced November 2023.
-
High-throughput assessment of the microstructural stability of segregation-engineered nanocrystalline Al-Ni-Y alloys
Authors:
W. Streit Cunningham,
Jungho Shin,
Tianjiao Lei,
Timothy J Rupert,
Daniel S. Gianola
Abstract:
Segregation engineering has emerged as a promising pathway towards designing thermally stable nanocrystalline alloys with enhanced mechanical properties. However, the compositional and processing space for solute stabilized microstructures is vast, thus the application of high-throughput techniques to accelerate optimal material development is increasingly attractive. In this work, combinatorial s…
▽ More
Segregation engineering has emerged as a promising pathway towards designing thermally stable nanocrystalline alloys with enhanced mechanical properties. However, the compositional and processing space for solute stabilized microstructures is vast, thus the application of high-throughput techniques to accelerate optimal material development is increasingly attractive. In this work, combinatorial synthesis is combined with high-throughput characterization techniques to explore microstructural transitions through annealing of a nanocrystalline ternary Al-base alloy containing a transition metal (TM=Ni) and rare earth dopant (RE=Y). A down-selected optimal composition with the highest thermal stability is annealed through in situ transmission electron microscopy, revealing that the removal of the RE species is correlated to a reduction in the microstructural stability at high temperatures as a result of variations in intermetallic phase formation. Results demonstrate the benefits of co-segregation for enhancing mechanical hardness and delaying the onset of microstructural instability.
△ Less
Submitted 30 August, 2023;
originally announced August 2023.
-
Grain Boundary Softening from Stress Assisted Helium Cavity Coalescence in Ultrafine-Grained Tungsten
Authors:
W. S. Cunningham,
Y. Zhang,
S. L. Thomas,
O. El-Atwani,
Y. Wang,
J. R. Trelewicz
Abstract:
The formation of helium cavities in coarse-grained materials produces hardening proportional to the number density and size of the cavities and due to the interaction of dislocations with intragranular helium defects. In nanostructured metals containing a high density of interfacial sinks, preferential cavity formation on the grain boundaries instead produces softening and often attributed to enha…
▽ More
The formation of helium cavities in coarse-grained materials produces hardening proportional to the number density and size of the cavities and due to the interaction of dislocations with intragranular helium defects. In nanostructured metals containing a high density of interfacial sinks, preferential cavity formation on the grain boundaries instead produces softening and often attributed to enhanced interfacial plasticity. Employing two grades of ultrafine-grained tungsten, we explore this effect using targeted implantation studies to map cavity evolution as a function of the irradiation conditions and quantify its impact on the mechanical response through nanoindentation. Softening is reported at implantation temperatures above the threshold for preferential grain boundary cavity formation but at a sufficiently low fluence prior to the growth of intragranular cavities. Collective changes in the mean cavity size, density, and morphology beneath a residual impression on an implanted surface indicate that cavity coalescence accompanied the reduction in hardness. Complementary atomistic simulations demonstrate that, in tungsten grain structures exhibiting softening, grain boundary bubble coalescence is driven by stress concentrations that further act to localize strain in the grain boundaries through cooperative deformation processes involving local atomic shuffling and sliding, dislocation emission, and even the nucleation of unstable twinning events.
△ Less
Submitted 27 March, 2023;
originally announced March 2023.