Oxide Membranes from Bulk Micro-Machining of SrTiO3 substrates
Authors:
Nicola Manca,
Alejandro Enrique Plaza,
Leonélio Cichetto Jr.,
Warner J. Venstra,
Cristina Bernini,
Daniele Marré,
Luca Pellegrino
Abstract:
Suspended micro-structures based on complex oxides relies on surface micro-machining processes such as those based on sacrificial layers. These processes prevent to physically access the microstructures from both sides, as substantial part of the substrate is not removed. In this work, we develop a bulk micromachining protocol of a commonly used substrate employed in oxide thin film deposition. We…
▽ More
Suspended micro-structures based on complex oxides relies on surface micro-machining processes such as those based on sacrificial layers. These processes prevent to physically access the microstructures from both sides, as substantial part of the substrate is not removed. In this work, we develop a bulk micromachining protocol of a commonly used substrate employed in oxide thin film deposition. We realize suspended oxide thin film devices by fabricating pass-through holes across SrTiO3(100) or SrTiO3(110) substrates. Careful calibration of anisotropic etching rates allows controlling the final geometry of the aperture in the substrate in a predictable way. As demonstrators of possible device geometries, we present clamped membranes and trampolines of (La,Sr)MnO3, a conductive magnetic oxide, and a suspended trampoline resonator carved from the SrTiO3 substrate itself. Reported protocols can be readily extended to a broad variety of other complex oxides so to extend the application of membranes technology beyond those of commercially-available silicon compounds.
△ Less
Submitted 9 October, 2024;
originally announced October 2024.
-
Solid lubrication by wet-transferred solution-processed graphene flakes: dissipation mechanisms and superlubricity in mesoscale contacts
Authors:
Renato Buzio,
Andrea Gerbi,
Cristina Bernini,
Luca Repetto,
Andrea Silva,
Andrea Vanossi
Abstract:
Solution-processed few-layers graphene flakes, dispensed to rotating and sliding contacts via liquid dispersions, are gaining increasing attention as friction modifiers to achieve low friction and wear at technologically-relevant interfaces. Vanishing friction states, i.e. superlubricity, have been documented for nearly-ideal nanoscale contacts lubricated by individual graphene flakes; there is ho…
▽ More
Solution-processed few-layers graphene flakes, dispensed to rotating and sliding contacts via liquid dispersions, are gaining increasing attention as friction modifiers to achieve low friction and wear at technologically-relevant interfaces. Vanishing friction states, i.e. superlubricity, have been documented for nearly-ideal nanoscale contacts lubricated by individual graphene flakes; there is however no clear understanding if superlubricity might persist for larger and morphologically-disordered contacts, as those typically obtained by graphene wet transfer from a liquid dispersion. In this study we address the friction performance of solution-processed graphene flakes by means of colloidal probe Atomic Force Microscopy. We use an additive-free aqueous dispersion to coat micrometric silica beads, which are then sled under ambient conditions against prototypical material substrates, namely graphite and the transition metal dichalcogenides (TMDs) MoS2 and WS2. High resolution microscopy proves that the random assembly of the wet-transferred flakes over the silica probes results into an inhomogeneous coating, formed by graphene patches that control contact mechanics through tens-of-nanometers tall protrusions. Atomic-scale friction force spectroscopy reveals that dissipation proceeds via stick-slip instabilities. Load-controlled transitions from dissipative stick-slip to superlubric continuous sliding may occur for the graphene-graphite homojunctions, whereas single- and multiple-slips dissipative dynamics characterizes the graphene-TMD heterojunctions. Systematic numerical simulations demonstrate that the thermally-activated single-asperity Prandtl-Tomlinson model comprehensively describes friction experiments involving different graphene-coated colloidal probes, material substrates and sliding regimes.
△ Less
Submitted 27 July, 2023;
originally announced July 2023.
-
Sliding friction and superlubricity of colloidal AFM probes coated by tribo-induced graphitic transfer layers
Authors:
Renato Buzio,
Andrea Gerbi,
Cristina Bernini,
Luca Repetto,
Andrea Vanossi
Abstract:
Colloidal probe Atomic Force Microscopy (AFM) allows to explore sliding friction phenomena in graphite contacts of nominal lateral size up to hundreds of nanometers. It is known that contact formation involves tribo-induced material transfer of graphite flakes from the graphitic substrate to the colloidal probe. In this context, sliding states with nearly-vanishing friction, i.e. superlubricity, m…
▽ More
Colloidal probe Atomic Force Microscopy (AFM) allows to explore sliding friction phenomena in graphite contacts of nominal lateral size up to hundreds of nanometers. It is known that contact formation involves tribo-induced material transfer of graphite flakes from the graphitic substrate to the colloidal probe. In this context, sliding states with nearly-vanishing friction, i.e. superlubricity, may set in. A comprehensive investigation of the transfer layer properties is mandatory to ascertain the origin of superlubricity. Here we explore the friction response of micrometric beads, of different size and pristine surface roughness, sliding on graphite under ambient conditions. We show that such tribosystems undergo a robust transition towards a low-adhesion, low-friction state dominated by mechanical interactions at one dominant tribo-induced nanocontact. Friction force spectroscopy reveals that the nanocontact can be superlubric or dissipative, in fact undergoing a load-driven transition from dissipative stick-slip to continuous superlubric sliding. This behavior is excellently described by the thermally-activated, single-asperity Prandtl-Tomlinson model. Our results indicate that upon formation of the transfer layer, friction depends on the energy landscape experienced by the topographically-highest tribo-induced nanoasperity. Consistently we find larger dissipation when the tribo-induced nanoasperity is sled against surfaces with higher atomic corrugation than graphite, like MoS2 and WS2, in prototypical Van der Waals layered hetero-junctions.
△ Less
Submitted 11 January, 2024; v1 submitted 3 October, 2022;
originally announced October 2022.
-
Graphite superlubricity enabled by triboinduced nanocontacts
Authors:
Renato Buzio,
Andrea Gerbi,
Cristina Bernini,
Luca Repetto,
Andrea Vanossi
Abstract:
Colloidal probe Atomic Force Microscopy allows to explore sliding states of vanishing friction, i.e. superlubricity, in mesoscopic graphite contacts. Superlubricity is known to appear upon formation of a triboinduced transfer layer, originated by material transfer of graphene flakes from the graphitic substrate to the colloidal probe. Previous studies suggest that friction vanishes due to crystall…
▽ More
Colloidal probe Atomic Force Microscopy allows to explore sliding states of vanishing friction, i.e. superlubricity, in mesoscopic graphite contacts. Superlubricity is known to appear upon formation of a triboinduced transfer layer, originated by material transfer of graphene flakes from the graphitic substrate to the colloidal probe. Previous studies suggest that friction vanishes due to crystalline incommensurability at the newly formed interface. However this picture still lacks several details, such as the roles of the tribolayer roughness and of loading conditions. Hereafter we gain deeper insight into the tribological response of micrometric silica beads sliding on graphite under ambient conditions. We show that the tribotransferred flakes behave as lubricious nanoasperities with a twofold role. First, they decrease the silica-graphite true contact area, in fact causing a breakdown of adhesion and friction by one order of magnitude. Second, they govern mechanical dissipation through the specific energy landscape experienced by the topographically-highest triboinduced nanoasperity. Remarkably, such contact junctions can undergo a load-driven atomic-scale transition from continuous superlubric sliding to dissipative stick-slip, that agrees with the single-asperity Prandtl-Tomlinson model. Superlubricity in mesoscopic silica-graphite junctions may therefore arise from the load-controlled competition between interfacial crystalline incommensurability and contact pinning effects at one dominant nanoasperity.
△ Less
Submitted 6 September, 2023; v1 submitted 7 September, 2021;
originally announced September 2021.
-
The role of etching anisotropy in the fabrication of freestanding oxide microstructures on SrTiO3(100), SrTiO3(110), and SrTiO3(111) substrates
Authors:
Alejandro Plaza,
Nicola Manca,
Cristina Bernini,
Daniele Marré,
Luca Pellegrino
Abstract:
The release process for the fabrication of freestanding oxide microstructures relies on appropriate, controllable and repeatable wet etching procedures. SrTiO3 is among the most employed substrates for oxide thin films growth and can be decomposed in HF:water solution. Such process is strongly anisotropic and is affected by local defects and substrate cut-plane. We analyze the etching behavior of…
▽ More
The release process for the fabrication of freestanding oxide microstructures relies on appropriate, controllable and repeatable wet etching procedures. SrTiO3 is among the most employed substrates for oxide thin films growth and can be decomposed in HF:water solution. Such process is strongly anisotropic and is affected by local defects and substrate cut-plane. We analyze the etching behavior of SrTiO3 substrates having (100), (110), and (111) cut-planes during immersion in a 5% HF:water solution. The etching process over the three substrates is compared in terms of pitting, anisotropy, macroscopic etch rate and underetching effects around HF-resistant (La,Sr)MnO3 thin film micropatterns. The release of targeted structures, such as the reported (La,Sr)MnO3 freestanding microbridges, depends on the substrate crystallographic symmetry and on the in-plane orientation of the structures themselves along the planar directions. By comparing the etching evolution at two different length scales, we distinguish two regimes for the propagation of the etching front: an intrinsic one, owning to a specific lattice direction, and a macroscopic one, resulting from the mixing of different etching fronts. We report the morphologies of the etched SrTiO3 surfaces and the geometries of the underetched regions as well as of the microbridge clamping zones. The reported analysis will enable the design of complex MEMS devices by allowing to model the evolution of the etching process required for the release of arbitrary structures made of oxide thin films deposited on top of STO.
△ Less
Submitted 20 July, 2021;
originally announced July 2021.
-
Synthesis and structural characterization of Sb-doped TiFe2Sn Heusler compounds
Authors:
M. Pani,
I. Pallecchi,
C. Bernini,
N. Ardoino,
D. Marré
Abstract:
Heusler compounds form a numerous class of intermetallics, which include two families of compositions ABC and AB2C, usually referred to as half- and full-Heusler compounds, respectively. Given their tunable electronic properties, made possible by adjusting the chemical composition, these materials are currently considered for the possible use in sustainable technologies such as solar energy and th…
▽ More
Heusler compounds form a numerous class of intermetallics, which include two families of compositions ABC and AB2C, usually referred to as half- and full-Heusler compounds, respectively. Given their tunable electronic properties, made possible by adjusting the chemical composition, these materials are currently considered for the possible use in sustainable technologies such as solar energy and thermoelectric conversion. According to theoretical predictions, Sb substitution in the TiFe2Sn full-Heusler compound is thought to yield band structure modifications that should enhance the thermoelectric power factor. In this work we tested the phase stability and the structural and microstructural properties of such heavily-doped compounds. We synthesized polycrystalline TiFe2Sn1-xSbx samples (x=0,0.1,0.2 and 1.0) by arc melting, followed annealing. The structural characterization, performed by x-ray powder diffraction and microscopy analyses, confirmed the formation of the Heusler AB2C structure (cF16, Fm-3m, prototype: MnCu2Al) in all samples, with only few percent amounts of secondary phases and only slight deviations from nominal stoichiometry. With increasing Sb substitution we found a steady decrease of the lattice parameter, confirming that the replacement takes place at the Sn site. Quite unusually, the as cast samples exhibited a higher lattice contraction than the annealed ones. The fully substituted x=1.0 compound, again adopting the MnCu2Al structure, does not form as stoichiometric phase and turned out to be strongly Fe deficient.The physical behavior at room temperature indicated that annealing with increasing temperature is beneficial for electrical and thermoelectrical transport. Moreover, we measured a slight improvement of electrical and thermoelectrical properties in the x=0.1 sample and a suppression in the x=0.2 sample, as compared to the undoped x=0 sample.
△ Less
Submitted 16 July, 2018; v1 submitted 12 July, 2018;
originally announced July 2018.
-
Ultralow friction of ink-jet printed graphene flakes
Authors:
R. Buzio,
A. Gerbi,
S. Uttiya,
C. Bernini,
A. E. Del Rio Castillo,
F. Palazon,
A. S. Siri,
V. Pellegrini,
L. Pellegrino,
F. Bonaccorso
Abstract:
We report the frictional response of few-layer graphene (FLG) flakes obtained by liquid phase exfoliation (LPE) of pristine graphite. To this end, we inkjet print FLG on bare and hexamethyldisilazane-terminated SiO2 substrates, producing micrometric patterns with nanoscopic roughness that are investigated by atomic force microscopy. Normal force spectroscopy and atomically resolved morphologies in…
▽ More
We report the frictional response of few-layer graphene (FLG) flakes obtained by liquid phase exfoliation (LPE) of pristine graphite. To this end, we inkjet print FLG on bare and hexamethyldisilazane-terminated SiO2 substrates, producing micrometric patterns with nanoscopic roughness that are investigated by atomic force microscopy. Normal force spectroscopy and atomically resolved morphologies indicate reduced surface contamination by solvents after a vacuum annealing procedure. Notably, the printed FLG flakes show ultralow friction comparable with micromechanically exfoliated graphene flakes. Lubricity is retained on flakes with lateral size of a few tens of nanometres, and with thickness as small as ~ 2 nm, confirming the high crystalline quality and low defects density in the FLG basal plane. Surface exposed step edges exhibit the highest friction values, representing preferential sites for originating secondary dissipative processes related to edge straining, wear or lateral displacement of the flakes. Our work demonstrates that LPE enables fundamental studies on graphene friction to the single-flake level. The capability to deliver ultralow-friction-graphene over technologically relevant substrates, using a scalable production route and a high-throughput, large-area printing technique, may also open up new opportunities in the lubrication of micro- and nano-electromechanical systems.
△ Less
Submitted 3 May, 2018;
originally announced May 2018.
-
Exploring the feasibility of Fe(Se,Te) conductors by ex-situ Powder-in-Tube method
Authors:
M. Palombo,
A. Malagoli,
M. Pani,
C. Bernini,
P. Manfrinetti,
A. Palenzona,
M. Putti
Abstract:
In this work, the feasibility condition of Powder-In-Tube (PIT) processed wires of Fe(Se,Te) superconductor has been investigated. We faced several technical issues that are extensively described and discussed. In particular, we tested different metals and alloys as external sheaths (Cu, Ag, Nb, Ta, Ni, Fe, cupronickel, brass) concluding that the only sheath that does not affect substantially the…
▽ More
In this work, the feasibility condition of Powder-In-Tube (PIT) processed wires of Fe(Se,Te) superconductor has been investigated. We faced several technical issues that are extensively described and discussed. In particular, we tested different metals and alloys as external sheaths (Cu, Ag, Nb, Ta, Ni, Fe, cupronickel, brass) concluding that the only sheath that does not affect substantially the Fe(Se,Te) phase is Fe. On the other hand, Fe sheath introduces excess iron in the Fe(Se,Te) phase, which affects the superconducting properties; we investigated the effects of the thermal treatments and of the powder composition in order to avoid it. The maximum Jc value obtained in our samples is 4*10^2 A/cm2, comparable to other published values of PIT conductors of the 11 family. We conclude that the fabrication of Fe(Se,Te) wires by PIT method is quite challenging and other approaches should be developed.
△ Less
Submitted 4 June, 2015;
originally announced June 2015.
-
Grain size determination of superconducting MgB2 powders from magnetization curve, image analysis and surface area measurement
Authors:
Maurizio Vignolo,
Gianmarco Bovone,
Emilio Bellingeri,
Cristina Bernini,
Gennaro Romano,
Mariateresa Buscaglia,
Vincenzo Buscaglia,
Antonio Sergio Siri
Abstract:
The present article reports a method for the average grain size evaluation of superconducting nano-particles through their magnetic properties. The use of SQUID magnetometry to determine the average MgB2 particle size was investigated and the results compared with those achieved through other techniques. In particular the data obtained from zero field cooled magnetization measurement as function o…
▽ More
The present article reports a method for the average grain size evaluation of superconducting nano-particles through their magnetic properties. The use of SQUID magnetometry to determine the average MgB2 particle size was investigated and the results compared with those achieved through other techniques. In particular the data obtained from zero field cooled magnetization measurement as function of the temperature were compared with the results obtained by scanning electron microscopy and Brunauer-Emmett-Teller techniques. The particle magnetization was measured by a commercial SQUID magnetometer in magnetic field (1 mT) and temperatures ranging from 5 to 50 K dispersing the powders in a grease medium. The grain size is obtained by fitting the data taking into account the Ginzburg-Landau temperature dependence of the London penetration depth. Variations on typical modeling parameters were explored in order to gain a better picture of the average grain size and the effectiveness of various measurement techniques. We find that it is possible to use the magnetization measurements to determine the average grain size even if the SEM image analysis allows extracting more information about the grain size distribution. Furthermore a Matlab routine has been developed in order to get automatic analysis of SEM images.
△ Less
Submitted 19 May, 2014;
originally announced May 2014.
-
In-situ high energy synchrotron X-ray diffraction investigation of the MgB2 phase formation and MgB2 tapes sintering
Authors:
Maurizio Vignolo,
Gennaro Romano,
Davide Nardelli,
Emilio Bellingeri,
Alberto Martinelli,
Alexey Bitchkov,
Cristina Bernini,
Andrea Malagoli,
Valeria Braccini,
Carlo Ferdeghini
Abstract:
In the present paper we report an in-situ high-energy X-ray diffraction analysis of MgB2 tapes during the preparation process. The experiment was performed in a specifically designed furnace working in reducing atmosphere, compatible with the Laue diffraction condition. The MgB2 synthesis was realized starting from MgH2 and amorphous B in powder form as precursors, varying reaction temperature and…
▽ More
In the present paper we report an in-situ high-energy X-ray diffraction analysis of MgB2 tapes during the preparation process. The experiment was performed in a specifically designed furnace working in reducing atmosphere, compatible with the Laue diffraction condition. The MgB2 synthesis was realized starting from MgH2 and amorphous B in powder form as precursors, varying reaction temperature and testing different cooling processes. We analyzed both the MgB2 synthesis and the sintering process of tapes prepared with these powders. Phase evolution, micro and crystallographic structure were monitored during the different thermal treatments. Among the main results we observed the formation of MgB2 at an extraordinary low temperature (300C), probably as a result of a solid-state reaction between MgH2 and B. Furthermore, we studied the dependence of the micro-structure upon the thermal treatment and its effect on the critical current performance of the superconducting tapes.
△ Less
Submitted 16 May, 2014;
originally announced May 2014.
-
A novel process to produce amorphous nano-sized B useful for MgB2 phase synthesis
Authors:
Maurizio Vignolo,
Gennaro Romano,
Cristina Bernini,
Alberto Martinelli,
Antonio Sergio Siri
Abstract:
In this paper we report a new synthesis route to produce boron powders characterized as being amorphous and having very fine particle size. This route has been developed to improve the performances of superconducting MgB2 powders, which can be directly synthesized from this nano-structured boron precursor by following the ex-situ or the in-situ P.I.T. method during the manufacturing of tapes, wire…
▽ More
In this paper we report a new synthesis route to produce boron powders characterized as being amorphous and having very fine particle size. This route has been developed to improve the performances of superconducting MgB2 powders, which can be directly synthesized from this nano-structured boron precursor by following the ex-situ or the in-situ P.I.T. method during the manufacturing of tapes, wires and cables. All the procedure steps are explained and the chemical-physical characterization of the boron powder, using x-ray diffraction (Xrd), scanning electron microscopy (SEM) and transmission electron microscopy (TEM) techniques, is reported. Furthermore, a comparison with commercial boron is given. Preliminary results of the magnetic and electrical characterization, such as the critical temperature (TC) and the transport critical current density (JC t), for the MgB2 tape are reported and compared with the tape prepared with commercial boron.
△ Less
Submitted 16 May, 2014;
originally announced May 2014.
-
High temperature heat treatment of B precursor and P.I.T. process optimization to increase Jc performances of MgB2-based conductor
Authors:
Maurizio Vignolo,
Gianmarco Bovone,
Cristina Bernini,
Shrikant Kawale,
Andrea Palenzona,
Gennaro Romano,
Antonio Sergio Siri
Abstract:
Promising results reported in our previous works led us to think that production of B powder plays a crucial role in MgB2 synthesis. A new method for boron preparation has been developed in our laboratory. This particular process is based on magnesiothermic reaction (Moissan process) with the addition of an initial step that gives boron powder with nano-metric grain size. In this paper we report o…
▽ More
Promising results reported in our previous works led us to think that production of B powder plays a crucial role in MgB2 synthesis. A new method for boron preparation has been developed in our laboratory. This particular process is based on magnesiothermic reaction (Moissan process) with the addition of an initial step that gives boron powder with nano-metric grain size. In this paper we report our efforts regarding optimization of PIT method for these nanometric powders and the resolution of problems previously highlighted such as the difficulty in powder packaging and the high friction phenomena occurring during cold working. This increases cracking during the tape and wire manufacturing leading to its failure. Packaging problems are related to the amorphous nature of boron synthesized in our laboratory, so a crystallization treatment was applied to improve crystallinity of B powder. To prevent excessive friction phenomena we synthesized non-stoichiometric MgB2 and using magnesium as lubricant. Our goal is the Jc improvement, but a global physical-chemical characterization was also made to analyze the improvement given by our treatments: this characterization includes X-ray diffraction, resistivity vs. temperature measurement, SEM image, besides magnetic and transport Jc measurements.
△ Less
Submitted 16 May, 2014;
originally announced May 2014.
-
Large critical current density improvement in Bi-2212 wires through groove-rolling process
Authors:
Andrea Malagoli,
Cristina Bernini,
Valeria Braccini,
Gennaro Romano,
Marina Putti,
Xavier Chaud,
Francois Debray
Abstract:
Recently the interest about Bi-2212 round wire superconductor for high magnetic field use has been enhancing despite the fact that an increase of the critical current is still needed to boost its successful use in such applications. Recent studies have demonstrated that the main obstacle to current flow, especially in long wires, is the residual porosity inside these Powder-In-Tube processed condu…
▽ More
Recently the interest about Bi-2212 round wire superconductor for high magnetic field use has been enhancing despite the fact that an increase of the critical current is still needed to boost its successful use in such applications. Recent studies have demonstrated that the main obstacle to current flow, especially in long wires, is the residual porosity inside these Powder-In-Tube processed conductors which develops in bubbles-agglomeration when the Bi-2212 melts. Through this work we tried to overcome this issue acting on the wire densification by changing the deformation process. Here we show the effects of groove-rolling versus drawing process on the critical current density JC and on the microstructure. In particular, groove-rolled multifilamentary wires show a JC increased by a factor of about 3 with respect to drawn wires prepared with the same Bi-2212 powder and architecture. We think that this approach in the deformation process is able to produce the required improvements both because the superconducting properties are enhanced and because it makes the fabrication process faster and cheaper.
△ Less
Submitted 13 February, 2013;
originally announced February 2013.
-
A new approach for improving global critical current density in Fe(Se0.5Te0.5) polycrystalline materials
Authors:
A. Palenzona,
A. Sala,
C. Bernini,
V. Braccini,
M. R. Cimberle,
C. Ferdeghini,
G. Lamura,
A. Martinelli,
I. Pallecchi,
G. Romano,
M. Tropeano,
R. Fittipaldi,
A. Vecchione,
A. Polyanskii,
F. Kametani,
M. Putti
Abstract:
A novel method to prepare bulk Fe(Se0.5Te0.5) samples is presented, based on a melting process and a subsequent annealing treatment. With respect to the standard sintering technique, it produces much more homogeneous and denser samples, characterized by large and well interconnected grains. The resulting samples exhibit optimal critical temperature values, sharp resistive and magnetic transitions,…
▽ More
A novel method to prepare bulk Fe(Se0.5Te0.5) samples is presented, based on a melting process and a subsequent annealing treatment. With respect to the standard sintering technique, it produces much more homogeneous and denser samples, characterized by large and well interconnected grains. The resulting samples exhibit optimal critical temperature values, sharp resistive and magnetic transitions, large magnetic hysteresis loops and high upper critical fields are observed. Interestingly, the global critical current density is much enhanced as compared to the values reported in literature for bulk samples of the same 11 family, reaching about 103 A/cm2 at zero field at 4.2 K as assessed by magnetic, transport and magneto-optical techniques. Even more importantly, its field dependence turns out to be very weak, such that at μ_{0}H = 7 T it is suppressed only by a factor \sim2.
△ Less
Submitted 21 May, 2012; v1 submitted 16 May, 2012;
originally announced May 2012.
-
Long- to short-range magnetic order in fluorine-doped CeFeAsO
Authors:
T. Shiroka,
G. Lamura,
S. Sanna,
G. Prando,
R. De Renzi,
M. Tropeano,
M. R. Cimberle,
A. Martinelli,
C. Bernini,
A. Palenzona,
R. Fittipaldi,
A. Vecchione,
P. Carretta,
A. S. Siri,
C. Ferdeghini,
M. Putti
Abstract:
The evolution of the antiferromagnetic order parameter in CeFeAsO_{1-x}F_{x} as a function of the fluorine content x was investigated primarily via zero-field muon-spin spectroscopy. The long-range magnetic order observed in the undoped compound gradually turns into a short-range order at x=0.04, seemingly accompanied/induced by a drastic reduction of the magnetic moment of the iron ions. Supercon…
▽ More
The evolution of the antiferromagnetic order parameter in CeFeAsO_{1-x}F_{x} as a function of the fluorine content x was investigated primarily via zero-field muon-spin spectroscopy. The long-range magnetic order observed in the undoped compound gradually turns into a short-range order at x=0.04, seemingly accompanied/induced by a drastic reduction of the magnetic moment of the iron ions. Superconductivity appears upon a further increase in doping (x>0.04) when, unlike in the cuprates, the Fe magnetic moments become even weaker. The resulting phase diagram evidences the presence of a crossover region, where the superconducting and the magnetic order parameters coexist on a nanoscopic range.
△ Less
Submitted 14 September, 2011;
originally announced September 2011.
-
Study of the MgB2 grain size role in ex-situ multifilamentary wires with thin filaments
Authors:
A. Malagoli,
V. Braccini,
C. Bernini,
G. Romano,
M. Vignolo,
C. Ferdeghini,
M. Putti
Abstract:
The MgB2 superconductor has already demonstrated its applicative potential, in particular for DC applications such as MRI magnets, thanks to the low costs of the raw materials and to its simple production process. However further efforts have still to be made in order to broaden its employment also towards the AC applications such as SFCL, motors, transformers. The main issues are related to the…
▽ More
The MgB2 superconductor has already demonstrated its applicative potential, in particular for DC applications such as MRI magnets, thanks to the low costs of the raw materials and to its simple production process. However further efforts have still to be made in order to broaden its employment also towards the AC applications such as SFCL, motors, transformers. The main issues are related to the reduction of the AC losses. Some of these can be faced by obtaining multifilamentary conductors with a large number of very fine filaments and, in this context, the powders granulometry can play a crucial role. We have prepared MgB2 starting powders with different granulometries and by the ex-situ P.I.T method we have realized multifilamentary wires with a number of filaments up to 361 and an average size of each filament lowered down to 30 microns. In particular we have studied the relationship between grain and filament size in terms of transport properties and show that the optimization of this ratio is possible in order to obtain suitable conductors for AC industrial applications.
△ Less
Submitted 16 November, 2009;
originally announced November 2009.
-
High-energy ball milling and synthesi temperature study to improve superconducting properties of MgB2 ex-situ tapes and wires
Authors:
Gennaro Romano,
Maurizio Vignolo,
Valeria Braccini,
Cristina Bernini,
Andrea Malagoli,
Matteo Tropeano,
Carlo Fanciulli,
Marina Putti,
Carlo Ferdeghini
Abstract:
MgB2 monofilamentary nickel-sheated tapes and wires were fabricated by means of the ex-situ powder-in-tube method using either high-energy ball milled and low temperature synthesized powders. All sample were sintered at 920 C in Ar flow. The milling time and the revolution speed were tuned in order to maximize the critical current density in field (Jc): the maximum Jc value of 6 x 10e4 A/cm2 at…
▽ More
MgB2 monofilamentary nickel-sheated tapes and wires were fabricated by means of the ex-situ powder-in-tube method using either high-energy ball milled and low temperature synthesized powders. All sample were sintered at 920 C in Ar flow. The milling time and the revolution speed were tuned in order to maximize the critical current density in field (Jc): the maximum Jc value of 6 x 10e4 A/cm2 at 5 K and 4 T was obtained corresponding to the tape prepared with powders milled for 144h at 180rpm. Vorious synthesis temperature were also investigated (730-900 C) finding a best Jc value for the wire prepared with powders synthesized at 745 C. We speculate that this optimal temperature is due to the fluidifying effect of unreacted magnesium content before the sintering process which could better connect the grains.
△ Less
Submitted 14 October, 2008;
originally announced October 2008.
-
Effect of grain refinement on enhancing critical current density and upper critical field in undoped MgB2 ex-situ tapes
Authors:
A. Malagoli,
V. Braccini,
M. Tropeano,
M. Vignolo,
C. Bernini,
C. Fanciulli,
G. Romano,
M. Putti,
C. Ferdeghini,
E. Mossang,
A. Polyanskii,
D. C. Larbalestier
Abstract:
Ex-situ Powder-In-Tube MgB2 tapes prepared with ball-milled, undoped powders showed a strong enhancement of the irreversibility field H*, the upper critical field Hc2 and the critical current density Jc(H) together with the suppression of the anisotropy of all of these quantities. Jc reached 104 A/cm2 at 4.2 K and 10 T, with an irreversibility field of about 14 T at 4.2 K, and Hc2 of 9 T at 25 K…
▽ More
Ex-situ Powder-In-Tube MgB2 tapes prepared with ball-milled, undoped powders showed a strong enhancement of the irreversibility field H*, the upper critical field Hc2 and the critical current density Jc(H) together with the suppression of the anisotropy of all of these quantities. Jc reached 104 A/cm2 at 4.2 K and 10 T, with an irreversibility field of about 14 T at 4.2 K, and Hc2 of 9 T at 25 K, high values for not-doped MgB2. The enhanced Jc and H* values are associated with significant grain refinement produced by milling of the MgB2 powder, which enhances grain boundary pinning, although at the same time also reducing the connectivity from about 12% to 8%. Although enhanced pinning and diminished connectivity are in opposition, the overall influence of ball milling on Jc is positive because the increased density of grains with a size comparable with the mean free path produces strong electron scattering that substantially increases Hc2, especially Hc2 perpendicular to the Mg and B planes.
△ Less
Submitted 25 July, 2008;
originally announced July 2008.
-
Superconducting and thermal properties of ex-situ Glidcop sheathed multifilamentary MgB2 wires
Authors:
A Malagoli,
M Tropeano,
V Cubeda,
C Bernini,
V Braccini,
C Fanciulli,
G Romano,
M Putti,
C Ferdeghini
Abstract:
In DC and AC practical applications of MgB2 superconducting wires an important role is represented by the material sheath which has to provide, among other things, a suitable electrical and thermal stabilization. A way to obtain a large enough amount of low resistivity material in to the conductor architecture is to use it as external sheath. In this paper we study ex-situ multifilamentary MgB2…
▽ More
In DC and AC practical applications of MgB2 superconducting wires an important role is represented by the material sheath which has to provide, among other things, a suitable electrical and thermal stabilization. A way to obtain a large enough amount of low resistivity material in to the conductor architecture is to use it as external sheath. In this paper we study ex-situ multifilamentary MgB2 wires using oxide-dispersion-strengthened copper (GlidCop) as external sheath in order to reach a good compromise between critical current density and thermal properties. We prepared three GlidCop samples differing by the content of dispersed sub-microscopic Al2O3 particles. We characterized the superconducting and thermal properties and we showed that the good thermal conductivity together the good mechanical properties and a reasonable critical current density make of GlidCop composite wire a useful conductor for applications where high thermal conductivity is request at temperature above 30K, such as Superconducting-FCL.
△ Less
Submitted 21 July, 2008;
originally announced July 2008.
-
Thermal properties of MgB2: the effect of disorder on gap amplitudes and relaxation times of p and s bands
Authors:
M. Putti,
E. Galleani,
I. Pallecchi,
C. Bernini,
P. Manfrinetti,
A. Palenzona,
M. Affronte
Abstract:
We present thermal conductivity and specific heat measurements on MgB2 and Mg-AlB2 samples. Thermal properties have been analysed by using a two-gap model in order to estimate the gap amplitudes, D(0)p and D(0)s and the intra-band scattering rates, Gss and Gpp. As a function of Al doping and disorder D(0)s rapidly decreases, while D(0)p is rather constant. Gss and Gpp are increased by the disord…
▽ More
We present thermal conductivity and specific heat measurements on MgB2 and Mg-AlB2 samples. Thermal properties have been analysed by using a two-gap model in order to estimate the gap amplitudes, D(0)p and D(0)s and the intra-band scattering rates, Gss and Gpp. As a function of Al doping and disorder D(0)s rapidly decreases, while D(0)p is rather constant. Gss and Gpp are increased by the disorder, being Gpp more affected than Gss.
△ Less
Submitted 5 June, 2003;
originally announced June 2003.
-
Upper critical fields of MgB2 thin films
Authors:
V. Ferrando,
C. Bernini,
P. Manfrinetti,
D. Marre',
M. Putti,
C. Tarantini,
C. Ferdeghini
Abstract:
Critical fields of four MgB2 thin films with a normal state resistivity ranging from 5 to 50 mWcm and Tc from 29.5 to 38.8 K were measured up to 28 T. Hc2(T) curves present a linear behavior towards low temperatures. Very high critical field values have been found, up to 24 T along the c-axis and 57 T in the basal plane not depending on the normal state resistivity values. In this paper, critica…
▽ More
Critical fields of four MgB2 thin films with a normal state resistivity ranging from 5 to 50 mWcm and Tc from 29.5 to 38.8 K were measured up to 28 T. Hc2(T) curves present a linear behavior towards low temperatures. Very high critical field values have been found, up to 24 T along the c-axis and 57 T in the basal plane not depending on the normal state resistivity values. In this paper, critical fields will be analyzed taking into account the multiband nature of MgB2; we will show that resistivity and upper critical fields can be ascribed to different scattering mechanisms.
△ Less
Submitted 22 April, 2003;
originally announced April 2003.